Transition metal complexes comprising carbene ligands serving as emitters for organic light-emitting diodes (OLED&#39;s)

ABSTRACT

Use of transition metal complexes of the formula (I) in organic light-emitting diodeswhere:M1 is a metal atom;carbene is a carbene ligand;L is a monoanionic or dianionic ligand;K is an uncharged monodentate or bidentate ligand selected from the group consisting of phosphines; CO; pyridines; nitriles and conjugated dienes which form a π complex with M1;n is the number of carbene ligands and is at least 1;m is the number of ligands L, where m can be 0 or ≥1;o is the number of ligands K, where o can be 0 or ≥1;where the sum n+m+o is dependent on the oxidation state and coordination number of the metal atom and on the denticity of the ligands carbene, L and K and also on the charge on the ligands carbene and L, with the proviso that n is at least 1, and alsoan OLED comprising these transition metal complexes, a light-emitting layer comprising these transition metal complexes, OLEDs comprising this light-emitting layer, devices comprising an OLED according to the present invention, and specific transition metal complexes comprising atb least two carbene ligands.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. patent applicationSer. No. 15/663,900, filed Jul. 31, 2017, now allowed, which is acontinuation of U.S. patent application Ser. No. 12/901,610, filed Oct.11, 2010, now U.S. Pat. No. 9,748,498, which is a divisional applicationof U.S. patent application Ser. No. 10/568,344, now U.S. Pat. No.7,846,763, which is a U.S. national phase application filed under 35U.S.C. § 371 claiming benefit to International ApplicationPCT/EP2004/009269, filed Aug. 18, 2004, which is entitled to priorityunder 35 U.S.C. § 119(a)-(d) to German Application No. 10338550.9, filedAug. 19, 2003, all of which applications are incorporated herein byreference in their entireties.

The present invention relates to the use of transition metal complexescomprising at least one carbene ligand in organic light-emitting diodes(OLEDs), a light-emitting layer, blocking layer for electrons orexcitons or blocking layer for holes comprising these transition metalcomplexes, OLEDs comprising these transition metal complexes, devicescomprising an OLED according to the present invention and also specifictransition metal complexes comprising at least two carbene ligands.

In organic light-emitting diodes (OLEDs), use is made of the ability ofmaterials to emit light when they are excited by an electric current.OLEDs are of particular interest as alternatives to cathode ray tubesand liquid crystal displays for producing flat VDUs. Owing to their verycompact construction and the intrinsically low power consumption,devices comprising OLEDs are particularly useful for mobileapplications, for example for use in mobile telephones, laptops, etc.

Numerous materials which emit light on excitation by an electric currenthave been proposed.

WO 02/15645 relates to OLEDs having a light-emitting layer whichcomprises phosphorescent transition metal compounds. The transitionmetal compounds display electrophosphoresence, especially in the blueregion of the visible electromagnetic spectrum. However, the colorcoordinates of the blue emitted by the complexes disclosed in WO02/15645 are in need of improvement.

WO 01/41512 relates to OLEDs having a light-emitting layer whichcomprises a molecule of the formula L₂MX, where M is particularlypreferably iridium and L is selected from the group consisting of2-(1-naphthyl)benzoxazole, 2-phenylbenzoxazole, 2-phenylbenzothiazole,7,8-benzoquinoline, coumarin, thienylpyridine, phenylpyridine,benzothienylpyridine, 3-methoxy-2-phenylpyridine and tolylpyridine and Xis selected from the group consisting of acetylacetonate,hexafluoroacetylacetonate, salicylidene, picolinate and8-hydroxyquinolinate.

WO 00/70655 relates to electroluminescent layers having a phosphorescentorganometallic iridium compound or osmium compound as light-emittingsubstance. Preference is given to tris(2-phenylpyridine)iridium aslight-emitting compound.

Although compounds which display electroluminescence in the blue, redand green regions of the electromagnetic spectrum are already known, theprovision of more efficient compounds which can be used industrially isdesirable. For the purposes of the present invention, the termelectroluminescence refers to both electrofluorescence andelectrophosphorescence. Furthermore, the provision of further compoundsfor use as materials which block electrons, excitons or holes is ofinterest.

It is an object of the present invention to provide a class of compoundswhich are suitable for producing electroluminescence in the blue, redand green regions of the electromagnetic spectrum, thus making theproduction of full-color displays possible. A further object of thepresent invention is to provide compounds for use as materials whichblock electrons, excitons or holes.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an organic light-emitting diode made up of a plurality oflayers.

FIG. 2 shows the crystal structure of the fac isomer of the Ir complex(7).

We have found that these objects are achieved by the use of unchargedtransition metal complexes of the formula I comprising at least onecarbene ligand in organic light-emitting diodes (OLEDs)

where the symbols have the following meanings:

-   -   M¹ is a metal atom selected from the group consisting of Co, Rh,        Ir, Nb, Pd, Pt, Fe, Ru, Os, Cr, Mo, W, Mn, Tc, Re, Cu, Ag and Au        in any oxidation state possible for the respective metal atom;    -   carbene is a carbene ligand which may be uncharged or        monoanionic and monodentate, bidentate or tridentate, with the        carbene ligand also being able to be a biscarbene or triscarbene        ligand;    -   L is a monoanionic or dianionic ligand, preferably a monoanionic        ligand, which may be monodentate or bidentate;    -   K is an uncharged monodentate or bidentate ligand selected from        the group consisting of phosphines, preferably        trialkylphosphines, triarylphosphines or alkylarylphosphines,        particularly preferably PAr₃, where Ar is a substituted or        unsubstituted aryl radical and the three aryl radicals in PAr₃        may be identical or different, particularly preferably PPh₃,        PEt₃, PnBu₃, PEt₂Ph, PMe₂Ph, PnBu₂Ph; phosphonates and        derivatives thereof, arsenates and derivatives thereof,        phosphites, CO; pyridines which may be substituted by alkyl or        aryl groups; nitriles and dienes which form a π complex with M¹,        preferably η⁴-diphenyl-1,3-butadiene, η⁴-1,3-pentadiene,        η⁴-1-phenyl-1,3-pentadiene, η⁴-1,4-dibenzyl-1,3-butadiene,        η⁴-2,4-hexadiene, η⁴-3-methyl-1,3-pentadiene,        η⁴-1,4-ditolyl-1,3-butadiene,        η⁴-1,4-bis(trimethylsilyl)-1,3-butadiene and η²- or        η⁴-cyclooctadiene (each 1,3 and 1,5), particularly preferably        1,4-diphenyl-1,3-butadiene, 1-phenyl-1,3-pentadiene,        2,4-hexa-diene, butadiene, η²-cyclooctene, η⁴-1,3-cyclooctadiene        and η⁴-1,5-cyclo-octadiene;    -   n is the number of carbene ligands, where n is at least 1 and        when n>1 the carbene ligands in the complex of the formula I can        be identical or different;    -   m is the number of ligands L, where m can be 0 or ≥1 and when        m>1 the ligands L can be identical or different;    -   o is the number of ligands K, where o can be 0 or ≥1 and when        o>1 the ligands K can be identical or different;        where the sum n+m+o is dependent on the oxidation state and        coordination number of the metal atom and on the denticity of        the ligands carbene, L and K and also on the charge on the        ligands carbene and L, with the proviso that n is at least 1.

The transition metal complexes of the formula I can be used in any layerof an OLED, with the ligand skeleton or central metal being able to bevaried to match it to desired properties of the metal complexes. Forexample, the transition metal complexes of the formula I can be used ina blocking layer for electrons, a blocking layer for excitons, ablocking layer for holes or the light-emitting layer of the OLED. Thecompounds of the formula I are preferably used as emitter molecules inOLEDs.

For the purposes of the present invention, a bidentate ligand is aligand which is coordinated at two points to the transition metal atomM¹.

For the purposes of the present invention a monodentate ligand is aligand which coordinates at one point of the ligand to the transitionmetal atom M¹.

Depending on the coordination number of the metal M¹ used and the natureand number of the ligands L, K and carbene used, various isomers of thecorresponding metal complexes can be present for the same metal M¹ andthe same nature and number of the ligands K, L and carbene used. Forexample, in the case of complexes of a metal M¹ which have thecoordination number 6 (i.e. octahedral complexes), for example Ir(III)complexes, both cis/trans isomers are possible when the complexes havethe general composition MA₂B₄, and fac/mer isomers (facial/meridionalisomers) are possible when the complexes have the general compositionMA₃B₃. In the case of square planar complexes of a metal M¹ which havethe coordination number 4, for example Pt(II) complexes, cis/transisomers are possible when the complexes have the general compositionMA₂B₂. The symbols A and B are each a binding point of a ligand, withnot only monodentate but also bidentate ligands being able to bepresent. An unsymmetrical bidentate ligand has, according to theabovementioned general composition, one group A and one group B.

A person skilled in the art will know what is meant by cis/trans orfac/mer isomers. In the case of octahedral complexes, the cis isomer ispresent in the case of complexes of the composition MA₂B₄ when the twogroups A occupy adjacent corners of an octahedron, while the two groupsA of the trans isomer occupy opposite corners of an octahedron. In thecase of complexes of the composition MA₃B₃, three groups of the sametype can occupy either the corners of one face of the octahedron (facialisomer) or a meridian, i.e. two of the three ligand bonding points arein trans positions relative to one another (meridional isomer). For thedefinition of cis/trans isomers and fac/mer isomers in octahedron metalcomplexes see, for example, J. Huheey, E. Keiter, R. Keiter,Anorganische Chemie: Prinzipien von Struktur und Reaktivität, 2nd,revised edition, translated and expanded by Ralf Steudel, Berlin; N.Y.:de Gruyter, 1995, pages 575, 576.

In the case of square planar complexes, the cis isomer is present in thecase of complexes of the composition MA₂B₂ when both the two groups Aand the two groups B occupy adjacent corners of a square, while in thetrans isomer both the two groups A and the two groups B in each caseoccupy the two diagonally opposite corners of a square. For thedefinition of cis/trans isomers in square planar metal complexes, see,for example, J. Huheey, E. Keiter, R, Keiter, Anorganische Chemie:Prinzipien von Struktur und Reaktivität, 2nd, revised edition,translated and expanded by Ralf Stendel, Berlin; N.Y.: de Gruyter, 1995,pages 557 to 559.

In general, the various isomers of the metal complexes of the formula Ican be separated by methods known to those skilled in the art, forexample by chromatography, sublimation or crystallization.

The present invention thus relates both to individual isomers of thetransition metal complexes of the formula I and to mixtures of variousisomeres in any mixing ratio.

Transition metal complexes which comprise carbene ligands are known fromthe prior art. Thus, Gründemann et al., J. Am. Chem. Soc., 2002, 124,10473 to 10481 and Danapoulos et al., J. Chem. Soc., Dalton Trans.,2002, 3090 to 3091, describe iridium complexes which have a carbeneligand comprising the following structural unit

Hitchcock et al. J. Organomet. Chem., 1982, 239, C 26-C 30, discloseiridium(III) complexes which have three monoanionic carbene ligands andpossess the following structural formula

However, none of the documents mentioned disclose luminescenceproperties, in particular electroluminescence properties, of thecompounds disclosed or their use in OLEDs.

Yam et al., Chem. Commun. 1989, 2261 to 2262 and Yam et al., J. Chem.Soc. Dalton Trans., 2001, 1911 to 1919, disclose ruthenium complexeswhich have a carbene ligand. The photophysical properties of thesecarbene complexes, including the photoluminescence of the complexes, wasexamined in the documents cited. However, nothing is said about use ofthese complexes, nor do the documents give information regarding theelectroluminescence of the compounds studied.

Che et al., Organometallics 1998, 17, 1622 to 1630, describe cationic Recomplexes having a carbene ligand comprising the following structuralunit

This complex displays photoluminescence. However, a use of the Recomplex or a study of the electroluminescence behavior of the complex isnot disclosed.

U.S. Pat. Nos. 6,160,267 and 6,338,977 relate to a molecularlight-emitting diode whose color changes as a function of the vaporssurrounding it. This electrode has a sensor-emitter layer comprising anuncharged platinum complex in which platinum is complexed by twonegatively charged ligands selected from the group consisting of CN⁻,NO₂ ⁻, NCO⁻, NCS⁻, Cl⁻, Br⁻, I⁻ and oxalate and the further two ligandsare selected from among at least one and at most two aryl isonitrilegroups and a Fischer carbene complex having the formula═C(Y)—NH—C₆H₄-alkyl, where Y is O-alkyl, NH-alkyl or N(alkyl)₂. Anecessary feature of the Pt complexes disclosed in U.S. Pat. Nos.6,160,267 and 6,338,977 is the presence of at least one aryl isonitrilegroup.

The suitability of transition metal complexes of the formula I accordingto the present invention which bear at least one carbene ligand aslight-emitting substances in OLEDs, with the substances of thisstructural type corresponding to the formula I being suitable forelectroluminescence in the red, green and blue regions of theelectromagnetic spectrum, is mentioned in none of the abovementioneddocuments.

It has thus been found that the transition metal complexes of theformula I as set forth in the present patent application are suitable aslight-emitting substances in OLEDs for producing full-color displays.

The transition metal complexes of the formula I used according to thepresent invention particularly preferably have a metal atom M¹ selectedfrom the group consisting of Os, Rh, Ir, Ru, Pd and Pt, with preferencebeing given to Os(IV), Rh(III), IR(I), Ir(III), Ru(III), Ru(IV), Pd(II)and Pt(II). Metal atoms which are particularly preferably used are Ru,Rh, Ir and Pt, preferably Ru(III), Ru(IV), Rh(III), IR(I), Ir(III) andPt(II). Very particular preference is given to using Ir or Pt,preferably Ir(III) or Pt(II), very particularly preferably Ir(III), asmetal atom M¹.

Suitable monoanionic or dianionic ligands L, preferably monoanionicligands L, which may be monodentate or bidentate are the ligandscustomarily used as monodentate or bidentate monoanionic or dianionicligands.

Suitable monoanionic monodentate ligands are, for example, halides, inparticular Cl⁻ and Br⁻, pseudohalides, in particular CN⁻,cyclopentadienyl (Cp⁻), alkyl radicals which are linked to thetransition metal M¹ via a sigma bond, for example CH₃, alkylarylradicals which are linked to the transition metal M¹ via a sigma bond,for example benzyl.

Suitable monoanionic bidentate ligands are, for example, acetylacetonateand its derivatives, picolinate, Schiff bases, amino acids and thebidentate monoanionic ligands mentioned in WO 02/15645, withacetylacetonate and picolinate being preferred.

Suitable uncharged monodentate or bidentate ligands have been mentionedabove. Preferred uncharged monodentate ligands are selected from thegroup consisting of PPh₃, P(OPh)₃, AsPh₃, CO, pyridine, nitriles andtheir derivatives. Particularly preferred uncharged monodentate orbidentate ligands are 1,4-diphenyl-1,3-butadiene,1-phenyl-1,3-pentadiene, 2,4-hexadiene, η⁴-cyclooctadiene andη²-cyclooctadiene (each 1,3 or 1,5).

The number n of the carbene ligands in uncharged transition metalcomplexes in which the transition metal atom Ir(III) has a coordinationnumber of 6 is from 1 to 3, preferably 2 or 3, particularly preferably3. If n>1, the carbene ligands can be identical or different, but arepreferably identical.

The number n of the carbene ligands in transition metal complexes inwhich the transition metal atom Pt(II) has a coordination number of 4 is1 or 2, preferably 2. If n is >1, the carbene ligands can be identicalor different.

The number m of monoanionic ligands L in the abovementioned case is from0 to 2, preferably 0 or 1, particularly preferably 0. If m>1, theligands L can be identical or different, but are preferably identical.

The number o of uncharged ligands K is dependent on whether thecoordination number 6 of the Ir(III) or 4 of the Pt(II) has been reachedby the total of carbene ligands and the ligands L. If, in the case whereIr(III) is used, n is three and three monoanionic bidentate carbeneligands are used, then o in the abovementioned case is 0. If, whenPt(II) is used, n is two and two monoanionic bidentate carbene ligandsare used, then o is in this case likewise 0.

In one embodiment, the present invention provides for the use oftransition metal complexes of the formula IA

where the symbols have the following meanings:

-   -   Do¹ is a donor atom selected from the group consisting of C, N,        O, P and S, preferably N, O, P and S, particularly preferably N;    -   r is 2, when Do¹ is C, is 1, when Do¹ is N or P and is 0 when        Do¹ is O or S;    -   Y¹, Y² are each, independently of one another, hydrogen or a        carbon-containing group selected from the group consisting of        alkyl, aryl, heteroaryl and alkenyl groups, preferably alkyl and        aryl groups,    -    or    -    Y¹ and Y² together form a bridge between the donor atom Do¹ and        the nitrogen atom N which has at least two atoms, preferably two        or three atoms, particularly preferably two atoms, of which at        least one is a carbon atom and the further atoms are preferably        nitrogen or carbon atoms, where the bridge may be saturated or        unsaturated, preferably unsaturated, and the two or more atoms        of the bridge can be substituted or unsubstituted;    -   Y³, Y⁴ are each, independently of one another, a hydrogen,        alkyl, aryl, heteroaryl or alkenyl radical; preferably hydrogen        or an alkyl, heteroaryl or aryl radical,        where Y¹, Y², Y³ and Y⁴ must not all at the same time be        hydrogen.

The symbols M¹, L, K and n, m and o have been mentioned above.

In the case of the groups Y1 and Y2, the following applies for thepurposes of the present patent application:

the substituents of the groups Y¹ and Y² can together form a bridgehaving a total of from three to five, preferably four, atoms of whichone or two atoms may be heteroatoms, preferably N, and the remainingatoms are carbon atoms, so that Y¹ and Y² together with this bridge forma five- to seven-membered, preferably six-membered, ring which may, ifappropriate, have two or, in the case of a six- or seven-membered ring,three double bonds and may, if appropriate, be substituted by alkyl oraryl groups and may, if appropriate, comprise heteroatoms, preferably N,with a six-membered aromatic ring which is substituted by alkyl or arylgroups or unsubstituted being preferred, or the preferred six-memberedaromatic ring is fused with further rings, preferably six-memberedaromatic rings, which may, if appropriate, comprise at least oneheteroatom, preferably N.

For the purposes of the present patent application, the terms arylradical or group, heteroaryl radical or group, alkyl radical or groupand alkenyl radical or group have the following meanings:

An aryl radical (or group) is a radical which has a basic skeletoncontaining from 6 to 30 carbon atoms, preferably from 6 to 18 carbonatoms, and is made up of an aromatic ring or a plurality of fusedaromatic rings. Suitable basic skeletons are, for example, phenyl,naphthyl, anthracenyl or phenanthrenyl. This basic skeleton can beunsubstituted (i.e. all carbon atoms which are able to be substitutedbear hydrogen atoms) or be substituted on one, more than one or allpositions capable of being substituted in the basic skeleton. Suitablesubstituents are, for example, alkyl radicals, preferably alkyl radicalshaving from 1 to 8 carbon atoms, particularly preferably methyl, ethylor i-propyl, aryl radicals, preferably C₆-aryl radicals, which may inturn be substituted or unsubstituted, heteroaryl radicals, preferablyheteroaryl radicals comprising at least one nitrogen atom, particularlypreferably pyridyl radicals, alkenyl radicals, preferably alkenylradicals containing one double bond, particularly preferably alkenylradicals having one double bond and from 1 to 8 carbon atoms, or groupswhich act as donors or acceptors. Donor groups are groups which have a+I and/or +M effect, and acceptor groups are groups which have a −Iand/or −M effect. Suitable groups which act as donors or acceptors arehalogen radicals, preferably F, Cl, Br, particularly preferably F,alkoxy radicals, aryloxy radicals, carbonyl radicals, ester radicals,amine radicals, amide radicals, CH₂F groups, CHF₂ groups, CF₃ groups, CNgroups, thio groups or SCN groups. The aryl radicals very particularlypreferably bear substituents selected from the group consisting ofmethyl, F, Cl, aryloxy and alkoxy. The aryl radical or the aryl group ispreferably a C₆-C₁₈-aryl radical, particularly preferably a C₆-arylradical which is optionally substituted by one or more of theabovementioned substituents. The C₆-C₁₈-aryl radical, preferably C₆-arylradical, particularly preferably bears one or two of the abovementionedsubstituents, with, in the case of a C₆-aryl radical, one substituentbeing located in the ortho, meta or para position relative to thefurther linkage point of the aryl radical and, in the case of twosubstituents, these can be located in the meta position or orthoposition relative to the further linkage point of the aryl radical orone radical is located in the ortho position and one radical is locatedin the meta position or one radical is located in the ortho or metaposition and the further radical is located in the para position.

A heteroaryl radical or a heteroaryl group is a radical which differsfrom the abovementioned aryl radicals in that at least one carbon atomin the basic skeleton of the aryl radical is replaced by a heteroatom.Preferred heteroatoms are N, O and S. Very particular preference isgiven to one or two carbon atoms of the basic skeleton of the arylradicals being replaced by heteroatoms. In particular, the basicskeleton is selected from among electron-rich systems such as pyridyland five-membered heteroaromatics such as pyrrole, furans. The basicskeleton can be substituted at one, more than one or all positions ofthe basic skeleton which are capable of being substituted. Suitablesubstituents are the same ones as those mentioned above for the arylgroups.

An alkyl radical or an alkyl group is a radical having from 1 to 20carbon atoms, preferably from 1 to 10 carbon atoms, particularlypreferably from 1 to 8 carbon atoms. This alkyl radical can be branchedor unbranched and may, if appropriate, be interrupted by one or moreheteroatoms, preferably Si, N, O or S, particularly preferably N, O orS. Furthermore, this alkyl radical can be substituted by one or more ofthe substituents mentioned for the aryl groups. It is likewise possiblefor the alkyl radical to bear one or more aryl groups. In this case, allof the abovementioned aryl groups are suitable. The alkyl radicals areparticularly preferably selected from the group consisting of methyl andof isopropyl.

An alkenyl radical or an alkenyl group is a radical which corresponds tothe abovementioned alkyl radicals having at least two carbon atoms, withthe difference that at least one C—C single bond of the alkyl radical isreplaced by a C—C double bond. The alkenyl radical preferably has one ortwo double bonds.

A bridge having at least two atoms of which at least one is a carbonatom and the further atoms are preferably nitrogen or carbon atoms,where the bridge can be saturated or preferably unsaturated and the twoor more atoms of the bridge may be substituted or unsubstituted, ispreferably one of the following groups:

-   -   A bridge having two carbon atoms or one carbon atom and one        nitrogen atom, where the carbon atoms or a carbon atom and a        nitrogen atom are joined by means of a double bond so that the        bridge has one of the following formulae, with the bridge        preferably having two carbon atoms:

-   -   R¹³ and R¹⁴ are each, independently of one another, hydrogen,        alkyl or aryl    -   or    -   R¹³ and R¹⁴ together form a bridge having a total of from 3 to        5, preferably 4, atoms of which one or two atoms may, if        appropriate, be heteroatoms, preferably N, and the remaining        atoms are carbon atoms, so that this group forms a 5- to        7-membered, preferably 6-membered, ring which may, if        appropriate, contain, in addition to the existing double bond,        one further double bond, or in the case of a 6- or 7-membered        ring two further double bonds, and may optionally be substituted        by alkyl or aryl groups. Preference is in this case given to a        six-membered aromatic ring. This may be substituted by alkyl or        aryl groups or be unsubstituted. Furthermore, it is possible for        one or more further aromatic rings to be fused onto this,        preferably six-membered, aromatic ring. In this case, any        conceivable fusion is possible. These fused-on radicals may in        turn be substituted, preferably by the radicals mentioned in the        general definition of the aryl radicals.    -   A bridge having two carbon atoms joined to one another by means        of a single bond, so that the bridge has the following formula:

where R⁴,

-   -   R⁵, R⁶    -   and R⁷ are each, independently of one another, hydrogen, alkyl,        aryl, heteroaryl or alkenyl, preferably hydrogen, alkyl or aryl.

M¹ in the transition metal complex of the formula IA is veryparticularly preferably Ir(III).

The group

is very particularly preferably selected from the group consisting of

where the symbols have the following meanings:

-   -   R⁴, R⁵, R⁶,    -   R⁷, R⁸, R⁹    -   and R¹¹ are each hydrogen, alkyl, aryl, heteroaryl, alkenyl or a        substituent which acts as a donor or acceptor and is preferably        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy radicals, aryloxy radicals,        carbonyl radicals, ester radicals, amine radicals, amide        radicals, CH₂F groups, CHF₂ groups, CF₃ groups, CN groups, thio        groups and SCN groups;    -   R¹⁰ is alkyl, aryl, heteroaryl, alkenyl, preferably alkyl,        heteroaryl or aryl, or 2 radicals R¹⁰ together form a fused-on        ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C⁶ ring, where one or more further aromatic rings may, if        appropriate, be fused on to this, preferably six-membered,        aromatic ring in any conceivable fashion and the fused-on        radicals may in turn be substituted; or R¹⁰ is a radical which        acts as a donor or acceptor, preferably selected from among        halogen radicals, preferably F, Cl, Br, particularly preferably        F; alkoxy, aryloxy, carbonyl, ester, amino groups, amide        radicals, CHF₂, CH₂F, CF₃, CN, thio groups and SCN;    -   v is from 0 to 4, preferably 0, 1 or 2, very particularly        preferably 0, where, when v is 0, all 4 possible substituents on        the aryl radical in formula c are hydrogen atoms.

The radicals Y³ and Y⁴ have been defined above.

In a further, preferred embodiment of the present invention, the carbeneligand or ligands in the uncharged transition metal complexes of theformula I is/are each a bidentate and/or monoanionic carbene ligand. Thecarbene ligand is very particularly preferably a monoanionic bidentatecarbene ligand.

The carbene ligand or ligands in the uncharged transition metal complexof the formula I very particularly preferably has/have the formula (II)

where the symbols have the following meanings:

-   -   Do¹ is a donor atom selected from the group consisting of C, P,        N, O and S, preferably P, N, O and S, particularly preferably N;    -   Do² is a donor atom selected from the group consisting of C, N,        P, O and S;    -   r is 2, when Do¹ is C, is 1 when Do¹ is N or P and is 0 when Do¹        is O or S;    -   s is 2 when Do² is C, is 1 when Do² is N or P and is 0 when Do²        is O or S;    -   X is a spacer selected from the group consisting of silylene,        alkylene, arylene, heteroarylene and alkenylene, preferably        alkylene or arylene, particularly preferably C₁-C₃-alkylene or        C₆-1,4-arylene, where at least one of the four further carbon        atoms may optionally be substituted by methyl, ethyl, n-propyl        or i-propyl groups or by groups which act as donors or acceptors        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy radicals, aryloxy radicals,        carbonyl, ester, amino groups, amide radicals, CHF₂, CH₂F, CF₃,        CN, thio groups and SCN; very particularly preferably methylene,        ethylene or 1,4-phenylene;    -   p is 0 or 1, preferably 0;    -   q is 0 or 1, preferably 0;    -   Y¹, Y² are each, independently of one another, hydrogen or a        carbon-containing group selected from the group consisting of        alkyl, aryl, heteroaryl and alkenyl groups; preferably alkyl,        heteroaryl and aryl groups;    -    or    -    Y¹ and Y² together form a bridge between the donor atom Do¹ and        the nitrogen atom N which has at least two atoms, preferably two        or three atoms, particularly preferably two atoms, of which at        least one is a carbon atom and the further atom or atoms is/are        each a nitrogen atom, where the bridge may be saturated or        unsaturated, preferably unsaturated, and the two or more atoms        of the bridge may be substituted or unsubstituted;    -   Y³ is hydrogen or an alkyl, aryl, heteroaryl or alkenyl radical,        preferably hydrogen or an alkyl, heteroaryl or an aryl radical,    -    or

-   -    where Do^(2′), q′, s′, R^(3′), R^(1′), R^(2′), X′ and p′ are        each, independently of one another, as defined for Do², q, s,        R³, R¹, R², X and p;    -   R¹, R² are each, independently of one another, hydrogen or an        alkyl, aryl, heteroaryl or alkenyl radical, preferably hydrogen,        an alkyl radical, a heteroaryl radical or an aryl radical;    -    or    -    R¹ and R² together form a bridge having a total of from three        to five, preferably four, atoms of which one or two atoms may be        heteroatoms, preferably N, and the remaining atoms are carbon        atoms, so that the group

-   -    forms a five- to seven-membered, preferably six-membered, ring        which may, if appropriate, contain, in addition to the existing        double bond, one further double bond or in the case of a six- or        seven-membered ring two further double bonds and may optionally        be substituted by alkyl or aryl groups and may, if appropriate,        comprise heteroatoms, preferably N, with a six-membered aromatic        ring which is substituted by alkyl or aryl groups or is        unsubstituted being preferred, or the preferred six-membered        aromatic ring is fused with further rings which may, if        appropriate, comprise at least one heteroatom, preferably N,        preferably six-membered aromatic rings;    -   R³ is hydrogen or an alkyl, aryl, heteroaryl or alkenyl radical,        preferably hydrogen or an alkyl, heteroaryl or aryl radical.

Preference is given to ligands of the formula II in which p and/or q are0, i.e. there are no spacers X and/or no donor atoms Doe present in theligands of the formula II.

The group

is preferably selected from the group consisting of

where the symbols have the following meanings:

-   -   R⁴, R⁵, R⁶,    -   R⁷, R⁸, R⁹    -   and R¹¹ are each hydrogen, alkyl, aryl, heteroaryl, alkenyl or a        substituent which acts as a donor or acceptor and is preferably        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy radicals, aryloxy radicals,        carbonyl radicals, ester radicals, amine radicals, amide        radicals, CH₂F groups, CHF₂ groups, CF₃ groups, CN groups, thio        groups and SCN groups, preferably hydrogen, alkyl, heteroaryl or        aryl;    -   R¹⁰ is alkyl, aryl, heteroaryl, alkenyl, preferably alkyl or        aryl, or 2 radicals R¹⁰ together form a fused-on ring which may,        if appropriate, comprise one or more heteroatoms, preferably N,        preferably form a fused-on aromatic C₆ ring, where one or more        further aromatic rings may, if appropriate, be fused on to this,        preferably six-membered, aromatic ring in any conceivable        fashion and the fused-on radicals may in turn be substituted; or        R¹⁰ is a radical which acts as a donor or acceptor, preferably        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F; alkoxy, aryloxy, carbonyl, ester,        amino groups, amide radicals, CHF₂, CH₂F, CF₃, CN, thio groups        and SCN;    -   v is from 0 to 4, preferably 0, 1 or 2, very particularly        preferably 0, where, when v is 0, all 4 possible carbon atoms on        the aryl radical in formula c which are optionally substituted        by R¹⁰ bear hydrogen atoms;    -   Y³ has been defined above.

The group

of the carbene ligand of the formula II is preferably

where the symbols have the following meanings:

-   -   Z is CH or N and can be located in the o, m or p position        relative to the point of linkage of the group to the carbene        ligand;    -   R¹² is an alkyl, aryl, heteroaryl or alkenyl radical, preferably        an alkyl or aryl radical, or 2 radicals R¹² together form a        fused-on ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C₆ ring, where one or more further aromatic rings may, if        appropriate, be fused onto this, preferably six-membered,        aromatic ring in any conceivable fashion, and the fused-on        radicals may in turn be substituted; or R¹² is a radical which        acts as a donor or acceptor, preferably selected from the group        consisting of halogen radicals, preferably F, Cl, Br,        particularly preferably F; alkoxy, aryloxy, carbonyl, ester,        amino groups, amide radicals, CHF₂, CH₂F, CF₃, CN, thio groups        and SCN;    -   t is 0 to 3 and when t>1 the radicals R¹² can be identical or        different; t is preferably 0 or 1 and when t is 1 the radical        R¹² is located in the ortho, meta or para position relative to        the point of linkage to the spacer X or, when p is 0, to the        point of linkage to the nitrogen atom adjacent to the carbene        carbon.

In the carbene ligands of the formula II, Y³ can be identical to ordifferent from the above-defined group and have one of the followingmeanings which have been mentioned above;

a hydrogen atom or an alkyl, aryl, heteroaryl or alkenyl radical,preferably a hydrogen atom or an alkyl, heteroaryl or aryl radical

or

where Do^(2′), q′, s′, R^(3′), R^(1′), R^(2′), X′ and p′ are each,independently of one another, defined as for Do², q, s, R³, R¹, R², Xand p.

Apart from carbene ligands of the formula II in which Y⁴, i.e. the groupof formula

is the structure

and Y³ is

carbene ligands in which Y⁴, i.e. the group of formula

is the structure

and Y³ isa hydrogen atom or an alkyl, aryl, heteroaryl or alkenyl radical,preferably a hydrogen atom or an alkyl, heteroaryl or aryl radical,are also suitable.

The definitions of the symbols correspond to the definitions givenabove.

The carbene ligand or ligands of the formula II is/are very particularlypreferably selected from the group consisting of

where the symbols have the following meanings:

-   -   Z, Z′ are identical or different and are each CH or N;    -   R¹², R^(12′) are identical or different and are each an alkyl,        aryl, heteroaryl or alkenyl radical, preferably an alkyl or aryl        radical, or 2 radicals R¹² or R^(12′) together form a fused-on        ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C₆ ring, where one or more further aromatic rings may, if        appropriate, be fused onto this, preferably six-membered,        aromatic ring in any conceivable fashion, and the fused-on        radicals may in turn be substituted; or R¹² or R^(12′) is a        radical which acts as a donor or acceptor, preferably selected        from the group consisting of halogen radicals, preferably F, Cl,        Br, particularly preferably F; alkoxy, aryloxy, carbonyl, ester,        amino groups, amide radicals, CHF₂, CH₂F, CF₃, CN, thio groups        and SCN;    -   t and t′ are identical or different, preferably identical, and        are each 0 to 3 and when t or t′>1 the radicals R¹² or R^(12′)        can be identical or different; t or t′ is preferably 0 or 1 and        when t or t′ is 1 the radical R¹² or R^(12′) is located in the        ortho, meta or para position relative to the point of linkage to        the nitrogen atom adjacent to the carbene carbon;    -   R⁴, R⁵, R⁶,    -   R⁷, R⁸, R⁹    -   and R¹¹ are each hydrogen, alkyl, aryl, heteroaryl, alkenyl or a        substituent which acts as a donor or acceptor and is preferably        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy radicals, aryloxy radicals,        carbonyl radicals, ester radicals, amine radicals, amide        radicals, CH₂F groups, CHF₂ groups, CF₃ groups, CN groups, thio        groups and SCN groups, preferably hydrogen, alkyl, heteroaryl or        aryl;    -   R¹⁰ is alkyl, aryl, heteroaryl, alkenyl, preferably alkyl,        heteroaryl or aryl, or 2 radicals R¹⁰ together form a fused-on        ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C₆ ring, where one or more further aromatic rings may, if        appropriate, be fused on to this, preferably six-membered,        aromatic ring in any conceivable fashion and the fused-on        radicals may in turn be substituted; or R¹⁰ is a radical which        acts as a donor or acceptor, preferably selected from among        halogen radicals, preferably F, Cl, Br, particularly preferably        F; alkoxy, aryloxy, carbonyl, ester, amino groups, amide        radicals, CHF₂, CH₂F, CF₃, CN, thio groups and SCN;    -   v is from 0 to 4, preferably 0, 1 or 2, very particularly        preferably 0, where, when v is 0, all 4 possible carbon atoms on        the aryl radical in formula c which are optionally substituted        by R¹⁰ bear hydrogen atoms.

Preferred transition metal complexes of the formula (I) are thus oneswhich comprise at least one carbene ligand of the formula II, withpreferred embodiments of the carbene ligand of the formula II havingbeen mentioned above.

Particularly preferred transition metal complexes of the formula I arethus ones which have the formula I(B)

The meanings of the symbols correspond to the meanings indicated abovein respect of the transition metal complex (I) and in respect of thecarbene ligand (II). Preferred embodiments have likewise been mentionedabove.

The transition metal complexes of the formula IB can, if a metal atom M¹having the coordination number 6 is used, be present as facial ormeridional isomer or as an isomer mixture of facial and meridionalisomers in any ratios when they have a composition MA³B³, as indicatedabove. Depending on the properties of the facial or meridional isomer ofthe transition metal complexes of the formula IB, preference can begiven to using either an isomerically pure facial isomer or anisomerically pure meridional isomer or an isomer mixture of facial andmeridional isomers in which one of the isomers is present in excess orthe two isomers are present in equal amounts. For example, facial andmeridional isomers of the transition metal complex of the formula IB arepossible when n is 3 and m and o are 0. When the transition metalcomplexes of the formula IB have a composition MA₂B₄, the transitionmetal complexes can be present in the form of cis/trans isomers in anyratios, as indicated above. Depending on the properties of the cis ortrans isomer of the transition metal complexes of the formula IB,preference can be given to using either an isomerically pure cis isomeror an isomerically pure trans isomer or an isomer mixture of cis andtrans isomers in which one of the isomers is present in excess or thetwo isomers are present in equal amounts. Cis/trans isomers of complexesof the formula IB are possible, for example, when M¹ is a metal atomhaving the coordination number 6 and when n is 2 and m is 2, in whichcase the two monodentate ligands L are identical, and o is 0 or when ois 2 and the two monodentate ligands K are identical and m is 0.

In the case of uncharged transition metal complexes in which thetransition metal atom is Ir(III) having a coordination number of 6, thenumber of the preferably monoanionic bidentate carbene ligands n is atleast 1 and not more than 3. The number of the preferred monoanionicbidentate carbene ligands is preferably 2 or 3, particularly preferably3. When n>1, the carbene ligands can be identical or different.

The transition metal complexes of the formula IB can, if a metal atom M¹having the coordination number 4 which forms square planar complexes isused, be present as cis or trans isomers or as an isomer mixture of cisand trans isomers in any ratios when they have a composition MA₂B₂, asindicated above. For example, cis/trans isomers of the transition metalcomplexes of the formula IB are possible when n is 2 and m and o are 0.

In the case of uncharged transition metal complexes in which thetransition metal atom is Pt(II) having a coordination number of 4, thenumber n of the preferred monoanionic bidentate carbene ligands n is 1or 2, preferably 2. When n=2, the carbene ligands can be identical ordifferent.

Very particular preference is given to a transition metal complex inwhich M¹ is Ir(III) having a coordination number of 6. In this Ir(III)complex, very particular preference is given to n being 3, m being 0, obeing 0, q being 0, p being 0, Do¹ being N and r being 1, with theremaining symbols being as defined above.

Especial preference is given to transition metal complexes of theformulae IBa to d selected from the group consisting of

where the symbols have the meanings indicated above in respect of thepreferred carbene ligands.

Among these Ir(III) complexes, very particular preference is given tothose of the formulae b, c and d. Especial preference is given toIr(III) complexes in which Z and Z′ are each CH, R⁸ and R⁹ are each H,t, t′ and v are each 0 and the remaining radicals have the meaningsindicated above in respect of the preferred carbene ligands.

The abovementioned uncharged transition metal complexes are very usefulas emitter molecules in organic light-emitting diodes (OLEDs). Simplevariations of the ligands or the central metal make it possible toprovide transition metal complexes which display electroluminescence inthe red, green or, in particular, blue region of the electromagneticspectrum. The uncharged transition metal complexes used according to thepresent invention are therefore suitable for use in industrially usablefull-color displays.

Furthermore, the abovementioned uncharged transition metal complexes aresuitable as electron blockers, exciton blockers or hole blockers inOLEDs, depending on the ligands used and the central metal used.

The present invention further provides uncharged transition metalcomplexes of the formula IC

where the symbols have the following meanings:

-   -   M¹ is Ru, Rh, Ir, Pt in any oxidation state possible for the        respective metal atom, preferably Ir or Pt;    -   L is a monoanionic or dianionic ligand, preferably a monoanionic        ligand, which may be monodentate or bidentate;    -   K is an uncharged monodentate or bidentate ligand;    -   n is the number of carbene ligands, where n is at least 2 and        the carbene ligands in the transition metal complex can be        identical or different;    -   m is the number of ligands L, where m can be 0 or ≥1 and when        m>1 the ligands L can be identical or different;    -   o is the number of ligands K, where o can be 0 or ≥1 and in the        case of o>1 the ligands K can be identical or different;        where the sum n+m+o is dependent on the oxidation state and        coordination number of the metal atom used and the denticity of        the ligands and also on the charge on the ligands, with the        proviso that n is at least 2;    -   Do² is a donor atom selected from the group consisting of C, N,        P, O and S;    -   s is 2 when Do² is C, is 1 when Do² is N or P and is 0 when Do²        is O or S;    -   X is a spacer selected from the group consisting of silylene,        alkylene, arylene, heteroarylene and alkenylene, preferably        alkylene or arylene, particularly preferably C₁-C₃-alkylene or        C₆-1,4-arylene, where at least one of the four further carbon        atoms may optionally be substituted by methyl, ethyl, n-propyl        or i-propyl groups or by groups which act as donors or acceptors        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy groups, aryloxy groups,        carbonyl groups, ester groups, amino groups, amide radicals,        CHF₂, CH₂F, CF₃, CN, thio groups and SCN; very particularly        preferably methylene, ethylene or 1,4-phenylene;    -   p is 0 or 1, preferably 0;    -   q is 0 or 1, preferably 0;    -   Y³ is hydrogen or an alkyl, aryl, heteroaryl or alkenyl radical,        preferably hydrogen or an alkyl or aryl radical,    -    or

-   -    where Do^(2′), q′, s′, R^(3′), R^(1′), R^(2′), X′ and p′ are        each, independently of one another, as defined for Do², q, s,        R³, R¹, R², X and p;    -   R¹, R² are each, independently of one another, hydrogen or an        alkyl, aryl, heteroaryl or alkenyl radical, preferably hydrogen,        an alkyl radical or aryl radical;    -    or    -    R¹ and R² together form a bridge having a total of from three        to five, preferably four, atoms of which one or two atoms may be        heteroatoms, preferably N, and the remaining atoms are carbon        atoms, so that the group

-   -    forms a five- to seven-membered, preferably six-membered, ring        which may, if appropriate, contain, in addition to the existing        double bond, one further double bond or in the case of a six- or        seven-membered ring two further double bonds and may optionally        be substituted by alkyl, heteroaryl or aryl groups and may, if        appropriate, comprise at least one heteroatom, preferably N,        with a six-membered aromatic ring which is substituted by alkyl        or aryl groups or is unsubstituted being preferred, or the        preferred six-membered aromatic ring is fused with further rings        which may, if appropriate, comprise at least one heteroatom,        preferably N, preferably six-membered aromatic rings;    -   R³ is hydrogen or an alkyl, aryl, heteroaryl or alkenyl radical,        preferably hydrogen or an alkyl, heteroaryl or aryl radical,

Y¹, Y² together form a bridge between the nitrogen atoms N which has atleast two atoms of which at least one is a carbon atom and the furtheratoms are preferably nitrogen or carbon atoms, where the bridge can besaturated or unsaturated and the two or more atoms of the bridge may besubstituted or unsubstituted and when the bridge has two carbon atomsand is saturated at least one of the two carbon atoms is substituted;where the bridge preferably has two atoms which may be substituted andis unsaturated.

Preferred and very particularly preferred embodiments of the symbols inthe novel transition metal complex of the formula IC have been mentionedabove in respect of the transition metal complexes used according to thepresent invention.

As a function of the substitution pattern on the central metal M¹ andwhen using a central metal having the coordination number 6, for exampleIr(III), the octahedral transition metal complexes can be present in theform of their facial or meridional isomers or as a mixture of facial andmeridional isomers in any ratios. The conditions for forming facial andmeridional isomers have been explained above. The present invention thuslikewise provides, apart from fac/mer isomer mixtures, the pure facialor meridional isomers of the transition metal complexes IC of theinvention, if these can occur as a result of the substitution pattern onthe central metal used. Depending on the properties of the facial ormeridional isomers of the transition metal complexes of the formula IB,preference can be given to using either an isomerically pure facialisomer or an isomerically pure meriodional isomer or an isomer mixtureof facial and meridional isomers in which one of the isomers is presentin excess or the two isomers are present in equal amounts. Theindividual isomers can be isolated from the corresponding isomer mixtureby, for example, chromatography, sublimation or crystallization.Appropriate methods of separating the isomers are known to those skilledin the art.

The group

in the transition metal complex IC of the present invention ispreferably selected from the group consisting of

where the symbols have the following meanings:

-   -   R⁴, R⁵, R⁶,    -   R⁷, R⁸, R⁹    -   and R¹¹ are each, independently of one another, hydrogen, alkyl,        aryl, heteroaryl, alkenyl or a substituent which acts as a donor        or acceptor and is preferably selected from among halogen        radicals, preferably F, Cl, Br, particularly preferably F,        alkoxy radicals, aryloxy radicals, carbonyl radicals, ester        radicals, amine radicals, amide radicals, CH₂F groups, CHF₂        groups, CF₃ groups, CN groups, thio groups and SCN groups,        preferably hydrogen, alkyl or aryl; where, in the formula a, at        least one of the radicals R⁴, R⁵, R⁶ and R⁷ is not hydrogen;    -   R¹⁰ is alkyl, aryl, heteroaryl, alkenyl, preferably alkyl or        aryl, or 2 radicals R¹⁰ together form a fused-on ring which may,        if appropriate, comprise one or more heteroatoms, preferably N,        preferably form a fused-on aromatic C₆ ring, where one or more        further aromatic rings may be fused on to this, preferably        six-membered, aromatic ring in any conceivable fashion and the        fused-on radicals may in turn be substituted; or R¹⁰ is a        radical which acts as a donor or acceptor, preferably selected        from among halogen radicals, preferably F, Cl, Br, particularly        preferably F; alkoxy, aryloxy, carbonyl, ester, amino groups,        amide radicals, CHF₂, CH₂F, CF₃, CN, thio groups and SCN;    -   v is from 0 to 4, preferably 0, 1 or 2, very particularly        preferably 0, where, when v is 0, all 4 possible carbon atoms on        the aryl radical in formula c which are optionally substituted        by R¹⁰ bear hydrogen atoms;    -   Y³ has been defined above.

The group

is preferably

where the symbols have the following meanings:

-   -   Z is CH or N and can be located in the o, m or p position        relative to the point of linkage of the group to the carbene        ligand;    -   R¹² is an alkyl, aryl, heteroaryl or alkenyl radical, preferably        an alkyl or aryl radical, or 2 radicals R¹² together form a        fused-on ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C₆ ring, where one or more further aromatic rings may, if        appropriate, be fused onto this, preferably six-membered,        aromatic ring in any conceivable fashion, and the fused-on        radicals may in turn be substituted; or R¹² is a radical which        acts as a donor or acceptor, preferably selected from the group        consisting of halogen radicals, preferably F, Cl, Br,        particularly preferably F; alkoxy, aryloxy, carbonyl, ester,        amino groups, amide radicals, CHF₂, CH₂F, CF₃, CN, thio groups        and SCN;    -   t is 0 to 3 and when t>1 the radicals R¹² can be identical or        different; t is preferably 0 or 1 and when t is 1 the radical        R¹² is located in the ortho, meta or para position relative to        the point of linkage to the spacer X or, when p is 0, to the        point of linkage to the nitrogen atom adjacent to the carbene        carbon.

Y³ can be identical to or different from the above-defined group.

The transition metal complex of the present invention particularlypreferably has at least two carbene ligands which are selectedindependently from the group consisting of

where the symbols have the following meanings:

-   -   Z, Z′ are identical or different, preferably identical, and are        each CH or N;    -   R¹², R^(12′) are identical or different, preferably identical,        and are each an alkyl, aryl, heteroaryl or alkenyl radical,        preferably an alkyl, heteroaryl or aryl radical, or 2 radicals        R¹² or R^(12′) together form a fused-on ring which may, if        appropriate, comprise one or more heteroatoms, preferably N,        preferably form a fused-on aromatic C₆ ring, where one or more        further aromatic rings may, if appropriate, be fused onto this,        preferably six-membered, aromatic ring in any conceivable        fashion, and the fused-on radicals may in turn be substituted;        or R¹² or R^(12′) is a radical which acts as a donor or        acceptor, preferably selected from the group consisting of        halogen radicals, preferably F, Cl, Br, particularly preferably        F; alkoxy, aryloxy, carbonyl, ester, amino groups, amide        radicals, CHF₂, CH₂F, CF₃, CN, thio groups and SCN;    -   t and t′ are identical or different, preferably identical, and        are each 0 to 3 and when t>1 the radicals R¹² or R^(12′) can be        identical or different; t or t′ is preferably 0 or 1 and when t        or t′ is 1 the radical R¹² or R^(12′) is located in the ortho,        meta or para position relative to the point of linkage to the        nitrogen atom adjacent to the carbene carbon;    -   R⁸, R⁹    -   and R¹¹ are each hydrogen, alkyl, aryl, heteroaryl, alkenyl or a        substituent which acts as a donor or acceptor and is preferably        selected from among halogen radicals, preferably F, Cl, Br,        particularly preferably F, alkoxy radicals, aryloxy radicals,        carbonyl radicals, ester radicals, amine radicals, amide        radicals, CH₂F groups, CHF₂ groups, CF₃ groups, CN groups, thio        groups and SCN groups, preferably hydrogen, alkyl or aryl;    -   R¹⁰ is alkyl, aryl, heteroaryl, alkenyl, preferably alkyl,        heteroaryl or aryl, or 2 radicals R¹⁰ together form a fused-on        ring which may, if appropriate, comprise one or more        heteroatoms, preferably N, preferably form a fused-on aromatic        C₆ ring, where one or more further aromatic rings may, if        appropriate, be fused on to this, preferably six-membered,        aromatic ring in any conceivable fashion and the fused-on        radicals may in turn be substituted; or R¹⁰ is a radical which        acts as a donor or acceptor, preferably selected from among        halogen radicals, preferably F, Cl, Br, particularly preferably        F; alkoxy, aryloxy, carbonyl, ester, amino groups, amide        radicals, CHF₂, CH₂F, CF₃, CN, thio groups and SCN;    -   v is from 0 to 4, preferably 0, 1 or 2, very particularly        preferably 0, where, when v is 0, all 4 possible carbon atoms on        the aryl radical in formula c which are optionally substituted        by R¹⁰ bear hydrogen atoms.

The novel transition metal complexes of the formula IC particularlypreferably contain a metal atom M¹ selected from the group consisting ofRh(III), Ir(III), Ru(III), Ru(IV) and Pt(II), preferably Pt(II) orIr(III). Particular preference is given to using Ir, preferably Ir(III),as metal atom M¹.

In a very particularly preferred embodiment, M¹ in the transition metalcomplexes of the present invention is Ir(III), n is 3 and m and o areeach 0 with particular preference being given to the three carbeneligands being identical.

The novel transition metal complexes of the formula IC can be preparedby methods analogous to those known to a person skilled in the art.Suitable preparative methods are described, for example, in the reviewarticles W. A. Hermann et al., Advances in Organometallic Chemistry,Vol. 48, 1 to 69, W. A. Hermann et al., Angew. Chem. 1997, 109, 2256 to2282 and G. Bertrand et al. Chem. Rev. 2000, 100, 39 to 91 and theliterature cited therein.

In one embodiment, the transition metal complexes of the presentinvention are prepared by deprotonation of the ligand precursorscorresponding to the appropriate carbene ligands and subsequent reactionwith suitable metal complexes comprising the desired metal. Thetransition metal complexes of the present invention can also be preparedby direct use of Wanzlick olefins.

Suitable ligand precursors are known to those skilled in the art. Theyare preferably cationic precursors.

In a preferred embodiment, the cationic precursors are deprotonated,which can result in different intermediates depending on the precursor.Thus, for example, alkoxide derivatives, dimeric Wanzlick olefins or thefree N-heterocycle carbenes can be formed depending on the way in whichthe reaction is carried out. Alkoxide derivatives and Wanzlick olefinsare preferably treated thermally in the presence of a suitable metalprecursor, resulting in elimination of the alcohol or dissociation ofthe dimer and formation of the metal-carbene compound in the presence ofsuitable metal complexes. If the free carbene is formed as intermediate,the reaction is preferably carried out with cooling and subsequentwarming to room temperature and, if necessary, further heating. Thereactions are preferably carried out in suitable solvents. In the caseof two-stage variants, the two substeps can be carried out using thesame solvent or different solvents. Suitable solvents are, for example,aromatic and aliphatic solvents or ethers, for example toluene,tetrahydrofuran. If free carbenes are not employed, it is also possibleto use alcohols or chlorinated hydrocarbons such as methylene chloride.To prepare free carbenes, it is also possible to use liquid ammonia, ifappropriate in admixture with tetrahydrofuran, as solvent.

The present invention therefore further provides a process for preparingthe novel transition metal complexes of the formula IC by deprotonationof the ligand precursors corresponding to the appropriate carbeneligands and subsequent reaction with suitable metal complexes comprisingthe desired metal.

The deprotonation of the ligand precursors can be carried out by meansof basic metalates, basic anions such as metal acetates,acetylacetonates or alkoxylates or external bases such as KO^(t)Bu,NaO^(t)Bu, LiO^(t)Bu, NaH, silylamides, amides and phosphazene bases.

The novel transition metal complexes of the formula IC bearingN-heterocyclic carbene ligands are preferably reacted by deprotonationof the appropriate cationic precursors selected from the groupconsisting of azolium salts, in particular imidazolium salts,benzimidazolium salts; triazolium salts and azolidinium salts, inparticular imidazolidinium salts, by means of an external base,preferably KO^(t)Bu or silylamines, particularly preferably silylamides,e.g. potassium bis(trimethylsilyl)amide. The intermediate obtained issubsequently reacted with a complex of the desired metal.

Suitable complexes of the desired metal are known to those skilled inthe art. The desired metal in the metal complex used and thecorresponding metal of the transition metal complex IC preparedtherefrom do not have to be in the same oxidation state.

In the preparation of iridium(III) complexes of the formula IC, whichare particularly preferred according to the present invention, it ispossible to use, for example, the following iridium(III) complexes:[(μ-Cl)Ir(η⁴-1,5-cod)]₂, [(μ-Cl)Ir(η²-1,5-coe)₂]₂, Ir(acac)₃, IrCl₃×nH₂O, (tht)₃IrCl₃, where cod is cyclooctadiene, coe is cyclooctene, acacis acetylacetonate and tht is tetrahydrothiophene.

The reaction is preferably carried out in a solvent. Suitable solventsare preferably selected from the group consisting of aromatic, aliphaticsolvents, ethers, alcohols and halogenated hydrocarbons. Alcohols andhalogenated hydrocarbons are generally used only when no free carbene isformed in the reaction. Furthermore, liquid ammonia can be used assolvent for generating free carbenes.

Alkoxide derivatives or Wanzlick olefins are usually added to theappropriate metal precursors at room temperature and subsequentlytreated thermally, which results in the corresponding alcohol beingeliminated in the case of the alkoxide derivatives or the dimericWanzlick olefins being dissociated and the metal-carbene compound beingformed. Temperatures of from 20 to 120° C., preferably from 25 to 110°C., are usually suitable for this reaction. If free carbenes are used asintermediates (e.g. imidazolin-2-ylidene), these are preferably firstlyadded to the metal precursor with cooling, after which the mixture iswarmed to room temperature (20-25° C.) and, if appropriate, subsequentlyheated further. Temperatures of from −78 to +120° C. are thus suitablefor this reaction.

The ratio of metal complex used to ligand precursor used is dependent onthe desired complex bearing at least two carbene ligands. If the metalatom is Ir(III), which is particularly preferred, and the desiredtransition metal complex comprises three carbene ligands, which islikewise particularly preferred, then the molar amount of ligandprecursors has to be about three times the molar amount of metal in themetal complex. A small excess of the ligand precursor can be used. Themolar ratio of metal in the metal complex to the molar amount of ligandprecursors is preferably from 1:3 to 1:5, particularly preferably from1:3 to 1:4.

The molar amount of the base used is dependent on the molar amount ofthe ligand precursor used; the base and the ligand precursor are used ina molar ratio of from 2:1 to 1:1, preferably from 1.5:1 to 1.2:1.

The preparation of two iridium complexes with N-heterocyclic carbeneligands according to the present invention is described below by way ofexample:

Imidazolinylidene complex:

X⁻ is an anionic group, preferably a halide, pseudohalide or anothermonoanionic group, for example Cl⁻, Br⁻, BF₄ ⁻, PF₆ ⁻, CN⁻, SCN⁻,particularly preferably BE₄ ⁻, PF₆ ⁻.

Benzimidazolinylidene complex:

X⁻ has been defined above.

The transition metal-carbene complexes used according to the presentinvention are very useful as emitter substances since they displayemission (electroluminescence) in the visible region of theelectromagnetic spectrum. The use of the transition metal-carbenecomplexes used according to the present invention as emitter substancesmakes it possible to provide compounds which display electroluminescencein the red, green or blue region of the electromagnetic spectrum. It isthus possible to obtain industrially usable full-color displays usingthe transition metal-carbene complexes used according to the presentinvention as emitter substances.

The ready availability of various substituted carbene ligands andvarious transition metals makes it possible to prepare emittersubstances which emit light in various regions of the electromagneticspectrum. The quantum yield is high and the stability of the transitionmetal-carbene complexes, in particular complexes bearing N-heterocycliccarbene ligands, in the device is high.

Furthermore, the abovementioned uncharged transition metal complexes aresuitable as electron blockers, exciton blockers or hole blockers inOLEDs, depending on the ligands used and the central metal used.

Organic light-emitting diodes are basically made up of a plurality oflayers. (Cf. FIG. 1 )

1. Anode

2. Hole transport layer

3. Light-emitting layer

4. Electron transport layer

5. Cathode

However, it is also possible for the OLED not to have all of the layersmentioned; for example, an OLED having the layers (1) (anode), (3)(light-emitting layer) and (5) (cathode) in which the functions of thelayers (2) (hole transport layer) and (4) (electron transport layer) aretaken over by the adjoining layers is likewise suitable. OLEDs havingthe layers (1), (2), (3) and (5) or the layers (1), (3), (4) and (5) arelikewise suitable.

The transition metal-carbene complexes according to the present patentapplication can be used in various layers of an OLED. The presentinvention therefore further provides an OLED comprising at least onetransition metal-carbene complex according to the present patentapplication. The transition metal-carbene complexes are preferably usedas emitter molecules in the light-emitting layer. The present inventiontherefore also provides a light-emitting layer comprising at least onetransition metal-carbene complex as emitter molecule. Preferredtransition metal-carbene complexes, in particular transitionmetal-carbene complexes bearing N-heterocyclic carbene ligands, havebeen mentioned above.

The transition metal-carbene complexes of the present invention or thoseused according to the present invention can be present in bulk, i.e.without further additives, in the light-emitting layer or another layerof the OLED, preferably in the light-emitting layer. However, it islikewise possible for further compounds in addition to the transitionmetal-carbene complexes used according to the present invention to bepresent in the layers comprising at least one transition metal-carbenecomplex according to the present patent application, preferably in thelight-emitting layer. For example, a fluorescent dye can be present inthe light-emitting layer in order to alter the emission color of thetransition metal-carbene complex used as emitted molecule. Furthermore,a diluent material can be used. This diluent material can be a polymer,for example poly(N-vinylcarbazole) or polysilane. However, the diluentmaterial can likewise be a small molecule, for example4,4′-N,N′-dicarbazolylbiphenyl (CDP═CBP) or tertiary aromatic amines. Ifa diluent material is used, the proportion of transition metal-carbenecomplexes used according to the present invention in the light-emittinglayer is generally less than 30% by weight, preferably less than 20% byweight, particularly preferably from 3 to 10% by weight.

The individual layers as described above of the OLEDs can in turn bemade up of 2 or more layers. For example, the hole transport layer canbe made up of a layer into which holes are injected from the electrodeand a layer which transports the holes from the hole injection layerinto the light-emitting layer. The electron transport layer can likewiseconsist of a plurality of layers, for example a layer into whichelectrons are injected by means of the electrode and a layer whichreceives electrons from the electron injection layer and transports themto the light-emitting layer. These layers are in each case selectedaccording to factors such as energy level, heat resistance and chargecarrier mobility and also the energy difference between the respectivelayer and the organic layers or the metal electrodes. A person skilledin the art will be able to select the structure of the OLEDs so that itis matched optimally to the transition metal-carbene complexes usedaccording to the present invention as emitter substances.

To obtain particularly efficient OLEDs, the HOMO (highest occupiedmolecular orbital) of the hole transport layer should be matched to thework function of the anode and the LUMO (lowest unoccupied molecularorbital) of the electron transport layer should be matched to the workfunction of the cathode.

The present invention further provides an OLED comprising at least onelight-emitting layer according to the present invention. The furtherlayers in the OLED can be made up of any material which is customarilyused in such layers and is known to those skilled in the art.

The anode (1) is an electrode which provides positive charge carriers.It can, for example, be made up of materials which comprise a metal, amixture of various metals, a metal alloy, a metal oxide or a mixture ofvarious metal oxides. As an alternative, the anode can be a conductivepolymer. Suitable metals comprise the metals of groups 11, 4, 5 and 6 ofthe Periodic Table of the Elements and the transition metals of groups 8to 10. If the anode is to allow light to pass through it, use isgenerally made of mixed oxides of metals of groups 12, 13 and 14 of thePeriodic Table of the Elements, for example indium-tin oxide (ITO). Itis likewise possible for the anode (1) to comprise an organic material,for example polyaniline, as described, for example, in Nature, Vol. 357,pages 477 to 479 (Jun. 11, 1992). At least one of the anode and cathodeshould be at least partially transparent to allow the light produced tobe emitted from the OLED.

Suitable hole transport materials for the layer (2) of the OLED of thepresent invention are disclosed, for example, in Kirk-OthmerEncyclopedia of Chemical Technology, 4^(th) Edition, Vol. 18, pages 837to 860, 1996. Both hole-transporting molecules and polymers can be usedas hole transport material. Hole-transporting molecules customarily usedare selected from the group consisting of4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (α-NPD),N,N′-diphenyl-N,N′-bis(3-methylphenyl)[1,1′-bi-phenyl-4,4′-diamine](TPD), 1,1-bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC),N,N′-bis(4-methylphenyl)-N,N′-bis(4-ethylphenyl)[1,1′-(3,3′-dimethyl)biphenyl-4,4′-di-amine](ETPD), N,N,N′,N′-tetrakis-(3-methylphenyl)phenylene-2,5-diamine (PDA),α-phenyl-4-N,N-diphenylaminostyrene (TPS), p-(diethylamino)benzaldehydediphenyl-hydrazone (DEH), triphenylamine (TPA),bis[4-(N,N-diethylamino)-2-methylphenyl)-(4-methylphenyl)methane (MPMP),1-phenyl-3-[p-(diethylamino)styryl]-5-[p-(diethyl-amino)phenyl]pyrazoline(PPR or DEASP), 1,2-trans-bis(9H-carbazol-9-yl)cyclobutane (DCZB),N,N,N′,N′-tetrakis(4-methylphenyl)-(1,1′-biphenyl)-4,4′-diamine (TTB)4,4′,4″-tris(N,N-diphenylamino)triphenylamine (TDTA) and porphyrincompounds and phthalocyanines such as copper phthalocyanines.Hole-transporting polymers customarily used are selected from the groupconsisting of polyvinylcarbazoles, (phenylmethyl)polysilanes, PEDOT(poly(3,4-ethylenedioxythiophene), preferably PEDOT doped with PSS(polystyrenesulfonate), and polyanilines. It is likewise possible toobtain hole-transporting polymers by doping polymers such as polystyreneand polycarbonate with hole-transporting molecules. Suitablehole-transporting molecules are the molecules which have been mentionedabove.

Suitable electron transport materials for the layer (4) of the OLEDs ofthe present invention comprise metal chelated with oxinoid compounds,e.g. tris(8-hydroxy-quinolato)aluminum (Alq₃), compounds based onphenanthroline, e.g. 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline(DDPA═BCP) or 4,7-diphenyl-1,10-phenanthroline (DPA), and azolecompounds such as 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxa-diazole(PBD) and 3-(4-biphenylyl)-4-phenyl-5-(4-t-butylphenyl)-1,2,4-triazole(TAZ). The layer (4) can either aid electron transport or serve asbuffer layer or barrier layer to avoid quenching of the excitons at theinterfaces of the layers of the OLED. The layer (4) preferably improvesthe mobility of the electrons and reduces quenching of the excitons.

Among the materials mentioned above as hole transport materials andelectron transport materials, some can perform a plurality of functions.For example, some of the electron-conducting materials simultaneouslyact as hole-blocking materials if they have a low HOMO.

The charge transport layers can also be electronically doped to improvethe transport properties of the materials used so as firstly to make thelayer thicknesses more generous (avoidance of pinholes/short circuits)and secondly to minimize the operating voltage of the device. Forexample, the hole transport materials can be doped with electronacceptors; e.g. phthalocyanines or arylamines such as TPD or TDTA can bedoped with tetrafluorotetracyanoquinodimethane (F4-TCNQ). The electrontransport materials can, for example, be doped with alkali metals; forexample, Alq₃ can be doped with lithium. Electronic doping is known tothose skilled in the art and is disclosed, for example, in W. Gao, A.Kahn, J. Appl. Phys., Vol. 94, No. 1, 1 Jul. 2003 (p-doped organiclayers); A. G. Werner, F. Li, K. Harada, M. Pfeiffer, T. Fritz, K. Leo,Appl. Phys. Lett., Vol. 82, No. 25, 23 Jun. 2003, and Pfeiffer et al.,Organic Electronics 2003, 4, 89-103.

The cathode (5) is an electrode which serves to introduce electrons ornegative charge carriers. The cathode can be any metal or nonmetal whichhas a lower work function than the cathode. Suitable materials for thecathode are selected from the group consisting of alkali metals of group1, for example Li, Cs, alkaline earth metals of group 2, metals of group12 of the Periodic Table of the Elements, comprising the rare earthmetals and the lanthanides and actinides. Furthermore, metals such asaluminum, indium, calcium, barium, samarium and magnesium and alsocombinations thereof can be used. In addition, lithium-comprisingorganometallic compounds or LiF can be applied between the organic layerand the cathode to reduce the operating voltage.

The OLED of the present invention can further comprise additional layersknown to those skilled in the art. For example, a layer which aidstransport of positive charges and/or fits the band gap of the layers toone another can be applied between the layer (2) and the light-emittinglayer (3). This further layer can alternatively serve as a protectivelayer. In an analogous manner, additional layers can be present betweenthe light-emitting layer (3) and the layer (4) to aid transport ofnegative charges and/or fit the band gap of the layers to one another.This layer can alternatively serve as protective layer.

In a preferred embodiment, the OLED of the present invention furthercomprises, in addition to the layers (1) to (5), at least one of thefollowing additional layers:

-   -   a hole injection layer between the anode (1) and the hole        transport layer (2);    -   a blocking layer for electrons and/or excitons between the hole        transport layer (2) and the light-emitting layer (3);    -   a blocking layer for holes and/or excitons between the        light-emitting layer (3) and the electron transport layer (4);    -   an electron injection layer between the electron transport        layer (4) and the cathode (5).

However, it is also possible for the OLED not to have all of theabovementioned layers (1) to (5); for example, an OLED having the layers(1) (anode), (3) (light-emitting layer) and (5) (cathode) in which thefunctions of the layers (2) (hole transport layer) and (4) (electrontransport layer) are taken over by the adjoining layers is likewisesuitable. OLEDs which have the layers (1), (2), (3) and (5) or thelayers (1), (3), (4) and (5) are likewise suitable.

A person skilled in the art will be familiar with the selection ofsuitable materials (for example on the basis of electrochemical tests).Suitable materials for the individual layers are known to those skilledin the art and disclosed, for example, in WO 00/70655.

Furthermore, each of the abovementioned layers of the OLED of thepresent invention can be made up of two or more layers. It is alsopossible for some or all of the layers (1), (2), (3), (4) and (5) tohave been surface-treated in order to increase the efficiency of chargecarrier transport. The materials for each of the layers mentioned arepreferably chosen so as to obtain an OLED having a high efficiency.

The OLED of the present invention can be produced by methods known tothose skilled in the art. In general, the OLED is produced by successivevapor deposition of the individual layers on a suitable substrate.Suitable substrates include, for example, glass or polymer films. Vapordeposition can be carried out using customary techniques such as thermalvaporization, chemical vapor deposition and others. In an alternativeprocess, the organic layers can be applied from solutions or dispersionsin suitable solvents using coating techniques known to those skilled inthe art. Compositions which comprise, in addition to the at least onetransition metal-carbene complex according to the invention, a polymericmaterial in one of the layers of the OLED, preferably in thelight-emitting layer, are generally applied as a layer by means ofsolution processing methods.

In general, the various layers have the following thicknesses: anode (2)500-5000 Å, preferably 1 000-2000 Å; hole transport layer (3) 50-1000 Å,preferably 200-800 Å, light-emitting layer (4) 10-1000 Å, preferably100-800 Å, electron transport layer (5) 50-1000 Å, preferably 200-800 Å,cathode (7) 200-10000 Å, preferably 300-5000 Å. The position of therecombination zone of holes and electrons in the OLED of the presentinvention and thus the emission spectrum of the OLED can be influencedby the relative thickness of the layers. This means that the thicknessof the electron transport layer should preferably be selected so thatthe electron/hole recombination zone is located in the light-emittinglayer. The ratio of the thicknesses of the individual layers in the OLEDis dependent on the materials used. The thicknesses of any additionallayers used are known to those skilled in the art.

Use of the transition metal-carbene complexes used according to thepresent invention in at least one layer of the OLED of the invention,preferably as emitter molecules in the light-emitting layer of the OLEDsof the present invention enables OLEDs having a high efficiency to beobtained. The efficiency of the OLEDs of the present invention can alsobe improved by optimizing the other layers. For example, high-efficiencycathodes such as Ca, Ba or LiF can be used. Shaped substrates and newhole transport materials which reduce the operating voltage or increasethe quantum efficiency can likewise be used in the OLEDs of the presentinvention. Furthermore, additional substances can be present in theOLEDs in order to adjust the energy level of the various layers and toassist electroluminescence.

The OLEDs of the present invention can be employed in all devices inwhich electroluminescence is useful. Suitable devices are preferablyselected from among stationary and mobile VDUs. Stationary VDUs include,for example, VDUs of computers, televisions, VDUs in printers, kitchenappliances and advertising signs, lighting units and information signs.Mobile VDUs include, for example, VDUs in mobile telephones, laptops,digital cameras, vehicles and destination displays on buses and trains.

Furthermore, the transition metal-carbene complexes used according tothe invention can be employed in OLEDs having an inverse structure. Inthese inverse OLEDs, the transition metal-carbene complexes are onceagain preferably used in the light-emitting layer. The structure ofinverse OLEDs and the materials customarily used therein are known tothose skilled in the art.

The above-described transition metal complexes of the present inventionor those used according to the present invention can not only beemployed in OLEDs but also as colorants which emit in the visible regionof the electromagnetic spectrum on irradiation with light(photoluminescence). Such colorants are preferably used as colorants inpolymeric materials.

The present invention therefore also provides for the use of theabove-described transition metal complexes of the present invention orthose used according to the present invention for coloring polymericmaterials.

Suitable polymeric materials include polyvinyl chloride, celluloseacetate, poly-carbonates, polyamides, polyurethanes, polyimides,polybenzimidazoles, melamine resins, silicones, polyesters, polyethers,polystyrene, polymethyl methacrylate, polyethylene, polypropylene,polyvinyl acetate, polyacrylonitrile, polybutadiene,polychlorobutadiene, polyisoprene and copolymers of the monomers listed.

Furthermore, the above-described transition metal complexes of thepresent invention or those used according to the present invention canbe employed in the following applications:

-   -   Use of the transition metal complexes as or in vat dye(s), for        example for coloring natural materials such as paper, wood,        straw, leather, pelts or natural fiber materials such as cotton,        wool, silk, jute, sisal, hemp, flax or animal hairs (for example        horsehair) and their conversion products such as viscose fibers,        nitrate silk or copper rayon (Reyon).    -   Use of the transition metal complexes as dyes, for example for        coloring paints, varnishes and other surface coating        compositions, paper colors, printing inks, inks and other colors        for drawing and writing purposes.    -   Use of the transition metal complexes as pigments, for example        for coloring paints, varnishes and other surface coating        compositions, paper colors, printing inks, inks and other colors        for drawing and writing purposes.    -   Use of the transition metal complexes as pigments in        electrophotography: for example for dry copying systems (Xerox        process) and laser printers.    -   Use of the transition metal complexes for safety marking        purposes in which good chemical and photochemical stability and        if appropriate also the luminescence of the substances is of        importance. This is preferably for checks, check cards, coupons        having a monetary value, documents, identification papers and        the like in which a particular, unmistakable color impression is        to be achieved.    -   Use of the transition metal complexes as additives to other        colors in which a particular color shade is to be achieved,        preferably particularly brilliant colors.    -   Use of the transition metal complexes for marking articles for        instrumental recognition of these articles by means of the        luminescence, preferably instrumental recognition of articles        for sorting purposes, for example in the recycling of plastics.    -   Use of the transition metal complexes as luminescent dyes for        machine-readable markings, preferably alphanumeric markings or        bar codes.    -   Use of the transition metal complexes for changing the frequency        of light, for example to convert short-wavelength light into        longer-wavelength, visible light.    -   Use of the transition metal complexes in display elements for a        wide variety of display, information and marking purposes, for        example in passive display elements, information signs and        traffic signs, e.g. traffic lights.    -   Use of the transition metal complexes in ink jet printers,        preferably in homogeneous solution as luminescent ink.    -   Use of the transition metal complexes as starting material for        superconducting organic materials.    -   Use of the transition metal complexes for solid-state        luminescent markings.    -   Use of the transition metal complexes for decorative purposes.    -   Use of the transition metal complexes for tracer purposes, for        example in biochemistry, medicine, engineering and natural        sciences. Here, the dyes can be bound covalently to substrates        or be bound via secondary valences such as hydrogen bonds or        hydrophobic interactions (adsorption).    -   Use of the transition metal complexes as luminescent dyes in        high-sensitivity detection methods (cf. C. Aubert, J.        Fünfschilling, I. Zschocke-Gränacher and H. Langhals, Z. Analyt.        Chem. 320 (1985) 361).    -   Use of the transition metal complexes as luminescent dyes in        scintillation devices.    -   Use of the transition metal complexes as dyes or luminescent        dyes in optical light-collection systems.    -   Use of the transition metal complexes as dyes or luminescent        dyes in luminescent solar collectors (cf. Langhals, Nachr. Chem.        Tech. Lab. 28 (1980) 716).    -   Use of the transition metal complexes as dyes or luminescent        dyes in luminescence-activated displays (cf. W. Greubel and G.        Baur, Elektronik 26 (1977) 6).    -   Use of the transition metal complexes as dyes or luminescent        dyes in cold light sources for light-induced polymerization for        the preparation of polymers.    -   Use of the transition metal complexes as dyes or luminescent        dyes for materials testing, for example in the production of        semiconductor circuits.    -   Use of the transition metal complexes as dyes or luminescent        dyes for the examination of microstructures of integrated        semiconductor components.    -   Use of the transition metal complexes as dyes or luminescent        dyes in photoconductors.    -   Use of the transition metal complexes as dyes or luminescent        dyes in photographic processes.    -   Use of the transition metal complexes as dyes or luminescent        dyes in display, illumination or image conversion systems in        which excitation occurs by means of electrons, ions or UV        radiation, for example in luminescent displays, Braun tubes or        in fluorescent tubes.    -   Use of the transition metal complexes as dyes or luminescent        dyes as part of an integrated semiconductor circuit, either as        such or in combination with other semiconductors, for example in        the form of epitaxy.    -   Use of the transition metal complexes as dyes or luminescent        dyes in chemiluminescence systems, for example in        chemiluminescent illumination rods, in immunoassays based on        luminescence or other detection methods based on luminescence.    -   Use of the transition metal complexes as dyes or luminescent        dyes as signal colors, for example for optical emphasis of        writing and drawings or other graphic products, for        individualizing signs and other articles in which a particular        optical color impression is to be achieved.    -   Use of the transition metal complexes as dyes or luminescent        dyes in dye lasers, for example as luminescent dyes for        generating laser beams.    -   Use of the transition metal complexes as active substances for        nonlinear optics, for example for frequency doubling and        frequency tripling of laser light.    -   Use of the transition metal complexes as rheology improvers.    -   Use of the transition metal complexes as dyes in photovoltaic        devices for converting electromagnetic radiation into electric        energy.

The following examples illustrate the invention.

EXAMPLES 1. Preparation of the Ligands

The necessary ligand precursors were prepared by methods based onliterature methods:

a) Compound (1)

The synthesis is carried out starting fromN,N-diphenylethane-1,2-diamine using a method based on that described inOrganic Letters, 1999, 1, 953-956; Angewandte Chemie, 2000, 112,1672-1674. The bisamine is reacted with triethyl formate in the presenceof ammonium tetrafluoroborate.

The compound was obtained after recrystallization from ethanol.

¹H-NMR (400 MHz, DMSO):

δ=4.60 (s, 4H, CH₂), 7.40 (tt, 2H), 7.57 (dd, 4H), 7.65 (dd, 4H), 9.95(s, 1H, C⁺H)

¹³C-NMR (100 MHz, DMSO):

δ=48.2, 118.4, 127.0, 129.6, 136.0, 151.7

b) Compound (2)

The synthesis starts, using a method based on that described in Chem.Ber. 1971, 104, 92-109 (in particular page 106), with the preparation ofthe bisimine of glyoxal and aniline or para-toluidine.

The Schiff bases obtained are converted into the correspondingimidazolium chloride salt by treatment with a hydrochloric acidsuspension of paraformaldehyde in dioxane using the method described inJournal of Organometallic Chemistry 2002, 606, 49-54.

Using aniline:

δ=7.64 (t,2H), 7.72 (t, 4H), 7.93 (d, 4H), 8.60 (d, 2H), 10.75 (s, 1H)

MS (ESI, ACN/H₂O 8/2):

m/e=221.0

Using para-toluidine:

¹H-NMR (500 MHz, DMSO): δ=2.42 (s, 6H), 7.49 (d, 4H), 7.88 (d, 4H), 8.61(d, 2H,), 10.52 (t, 1H)

The anion can be replaced by treatment with AgBF₄ or NaBF₄.

c) Compound (3)

The synthesis starts out from 1,2-phenylenediamine. After introductionof acetyl groups on the amino functions, the phenyl groups wereintroduced into the resulting amide with the aid of a copper-catalyzedprocedure as described in Synthetic Communications, 2000, 30, 3651-3668.Without purification, the material was treated in boiling ethanolic KOHsolution. The product was obtained by chromatography.

¹H-NMR (CD₂Cl₂, 500 MHz):

δ=5.70 (s, broad, 2H), 6.87 (t, 2H), 6.93 (d, 4H), 6.97 (dd, 2H), 7.22(t, 4H), 7.28 (dd, 2H)

The imidazolium salt required was prepared by treatment ofN,N′-diphenylbenzene-1,2-diamine with triethyl orthoformate in thepresence of ammonium tetrafluoroborate. The material was obtained bycrystallization.

¹H-NMR (DMSO, 400 MHz):

δ=7.74-7.84 (m, 8H), 7.91-7.98 (m, 6H), 10.57 (s, 1H)

d) Compound (4) da) Preparation of Compound 4a

In a countercurrent of argon, 3.16 g (20 mmol) of 2,3-diaminonaphthalene(Acros) and 6.28 g (40 mmol) of distilled bromobenzene (Aldrich)together with 80 ml of toluene (water-free) were placed in a flask whichhad been flushed with argon. The brown suspension was degassed byapplication of a vacuum to the flask. Argon was then admitted again anda spatula tip of Pd₂(dba)₃, a spatula tip of9,9-dimethyl-4,5-bis-(diphenylphosphino)xanthene (xantphos), 2.70 g (28mmol) of sodium tert-butoxide and 0.36 g (20 mmol) of degassed waterwere added in a countercurrent of argon. The brown suspension was heatedto reflux and stirred under reflux for 15 hours. It was then allowed tocome to room temperature.

For the work-up, the mixture was diluted with methylene chloride andextracted twice with water, then dried over sodium sulfate, filtered andthe filtrate was evaporated under reduced pressure. The residue waspurified by column chromatography (silica gel, methylene chloridecomprising 5 ml of triethylamine per I of methylene chloride). Thefractions comprising the product were combined and freed of the solventunder reduced pressure. This gave 2.7 g (43.5%) of compound (4a).

¹H-NMR (CDCl₃, 400 MHz):

δ=5.85 (s, broad, NH), 6.97 (tt, 2H, J=7.3 Hz, J=1.2 Hz), 7.07 (dd, 4H,J=8.7 Hz, J=1.1 Hz), 7.28-7.32 (m, 6H), 7.60 (dd, 2H, J=6.1 Hz, J=3.1Hz), 7.64 (s, 2H)

MS (EI):

m/e=310.0, 311.0, 312.0 (M⁺)

db) Preparation of Compound (4)

A two-neck flask was flushed with nitrogen for 20 minutes. 7.68 g (24.74mmol) of the 2,3-di-N-phenylaminonaphthalene were then dissolved in51.34 g (346.4 mmol) of triethyl formate at 100° C. and 2.59 g (24.74mmol) of ammonium tetrafluoroborate were added, also under acountercurrent of nitrogen. The solution was then heated to reflux andstirred under reflux for 12 hours. The reaction mixture was then broughtto room temperature.

For the work-up, the reaction mixture was filtered through a G4 frit andthe solid was washed with ortho ester. It was then dried at 50° C. in avacuum drying oven. The material obtained in this way (6.05 g) wasdissolved in methylene chloride and filtered by means of a suctionfilter. The mother liquor was evaporated under reduced pressure and thesolid was once again dried at 50° C. in a vacuum drying oven. This gave5.37 g (53%) of the compound (4).

¹H-NMR (0114600902, 400 MHz, CD₂Cl₂):

δ=7.69 (dd, 2H, J 2.9 Hz, J=6.7 Hz), 7.76-7.82 (m, 6H), 7.91-7.95 (m,4H), 8.10 (dd, 2H, J=3.3 Hz, J=6.6 Hz), 8.29 (s, somewhat broader, 2H),9.75 (s, 1H)

Elemental analysis:

Exp. 18.3% F 67.2% C 6.8% N 4.10% H Theor. 18.6% F 67.6% C 6.8% N 4.16%H

2. Preparation of the Metal Complexes

Ir(imidazolidine)₃ was prepared by a method based on that of P. B.Hitchcock, M. F. Lappert, P. Terreros, J. Organomet. Chem. 1982, 239,C26-C30. Unlike the literature method cited, the imidazolidinium saltrather than the Wanzlick olefin was used as starting material.

Preparation of the metal-carbene complexes (all syntheses described werecarried out in pure solvents under an inert gas atmosphere by means ofthe Schlenk technique):

a) Preparation of an Ir Complex (5)

In a 100 ml three-necked flask, 3.0 g (9.6 mmol) of the imidazolium salt(compound (1)) were suspended in 40 ml of tetrahydrofuran. Thelight-brown suspension was admixed at room temperature with a solutionof 1.11 g (9.7 mmol) of KO^(t)Bu in 10 ml of THF. The mixture wasstirred at room temperature for one hour and subsequently evaporated todryness. After the solid had been taken up again in 30 ml of toluene,the resulting suspension was added to a solution of 820 mg (1.2 mmol) of[(μ-Cl)(η⁴-1,5-cod)Ir]₂ in 20 ml of toluene. The reaction mixture wasrefluxed for 2 hours, stirred overnight at room temperature andsubsequently refluxed for another 3.5 hours. It was then allowed to coolto room temperature. The precipitate was filtered off, washed withtoluene, extracted with methylene chloride and the methylene chloridewas removed under reduced pressure. The residue was subjected topurification by column chromatography. This gave a light-yellow powder(240 mg, 15%).

¹³C-NMR (CD₂Cl₂, 125 MHz): 200.0 (NCN), 149.3, 146.5, 142.5 (each C_(q)or IrC_(phenyl)), 134.5, 127.2, 126.5, 125.5, 120.6, 119.7, 106.8 (eachCH_(phenyl)), 53.8, 44.1 (NCH₂CH₂N).

Mass (EI): m/e=856.

Optical spectroscopy: λ=533 nm (main maximum of the powder).

b) Preparation of an Ir Complex (6)

In a 100 ml three-necked flask, 0.92 g (2.7 mmol) of the imidazoliumsalt (compound (2)) was dissolved in 20 ml of tetrahydrofuran. At −8°C., 547 ml of base (0.5 M in toluene, 2.8 mmol) were added over a periodof 10 minutes and the mixture was stirred at room temperature for 1hour.

310 mg (0.460 mmol) of [(μ-Cl)(η⁴-1,5-cod)Ir]₂ were dissolved in 20 mlof THF, cooled to −78° C. and the salt mixture was added dropwise tothis solution. The mixture was stirred for 2 hours at 60° C., overnightat room temperature, for 8 hours under reflux and subsequently overnightat room temperature. After filtration, the solution was evaporated todryness and the brown residue was subjected to purification by columnchromatography. This gave a white powder (170 mg, 20%).

¹H-NMR (CD₂Cl₂, 500 MHz): 7.23 (1H, CH_(phenyl) or NCHCHN), 7.02 (1H),6.79 (2H), 6.68 (1H), 6.30 (2H), 5.85 (2H) (each CH_(phenyl) or NCHCHN),2.21 (3H, CH₃), 2.01 (3H, CH₃).

¹³C-NMR (CD₂Cl₂, 125 MHz): 174.8 (NCN), 149.3, 144.2, 137.6, 135.7,132.3 (each C_(q) or IrC_(phenyl)), 139.6, 127.8, 125.0, 120.2, 120.0,113.4, 109.1 (CH_(phenyl) or NCHCHN), 20.5, 19.9 (each CH₃).

Mass (EI): m/e=934.

Optical spectroscopy: λ=489 nm (main maximum of the powder).

c) Preparation of an Ir Complex (7) Synthesis Variant I

In a 100 ml three-necked flask, 0.99 g (2.8 mmol) of the benzimidazoliumsalt (compound (3)) was suspended in 20 ml of THF. A solution of 0.32 gof KO^(t)Bu in 10 ml of THF was added to this light yellow suspension atroom temperature. The mixture was stirred at room temperature for 45minutes and subsequently evaporated to dryness. After the residue hadbeen taken up again in 25 ml of toluene, this suspension was added to asolution of 310 mg of [(μ-Cl)(η⁴-1,5-cod)Ir]₂ (0.46 mmol) in 30 ml oftoluene. The mixture was subsequently stirred for 15 minutes at roomtemperature, overnight at 80° C., for 8 hours under reflux, over theweekend at room temperature and for 5 hours under reflux. After cooling,the precipitate was separated off and the filtrate was evaporated. Theyellow powder obtained was subjected to purification by columnchromatography. This gave a white powder (410 mg, 43%)

Synthesis Variant II

1.32 g (3.7 mmol) of the benzimidazolium salt (compound (3)) togetherwith 25 ml of toluene were placed in a 100 ml three-neck flask. 7.5 mlof potassium bistrimethyl-silylamide (0.5 M in toluene, 3.7 mmol) wereadded at room temperature over a period of 30 minutes and the mixturewas stirred at room temperature for 30 minutes. 310 mg (0.46 mmol) of[(μ-Cl)(η⁴-1,5-cod)Ir]₂ were dissolved in 30 ml of toluene and the saltmixture was added dropwise at room temperature. The mixture was stirredat room temperature for one hour, then at 70° C. for two hours andsubsequently overnight under reflux. After filtration, the solution wasevaporated to dryness and the brown residue was subjected topurification by column chromatography. This gave a white powder (0.75 g,82%).

The Ir complex (7) is formed as a mixture of the kinetically preferredmeridional (mer) isomer and the thermodynamically preferred facial (fac)isomer.

¹H-NMR (fac/mer isomer mixture, data for the main isomer (fac isomer),CDCl₃, 500 MHz): 8.03 (d, 1H), 7.85 (d, 1H), 7.21 (m, 2H), 7.01 (m, 1H),6.93 (m, 1H), 6.65 (m, 1H), 6.61 (m, 1H), 6.53 (m, 1H), 6.47 (m, 1H),6.35 (d, 1H), 6.20 (m, 1H), 6.11 (m, 1H) each (CH_(aryl) or NCHCHN).

¹³C-NMR (fac/mer isomer mixture, data for the main isomer (fac isomer),CDCl₃, MHz): 187.8 (NCN), 148.8, 147.8, 137.2, 136.9, 131.7 (each C_(q)or IrC_(phenyl)), 135.9, 127.8, 127.3, 127.0, 126.6, 126.4, 123.6,121.9, 120.8, 120.3, 111.6, 109.9, 109.5 (CH_(aryl)).

Mass (fac/mer isomer mixture, EI): m/e=1000.0.

Elemental analysis (fac/mer isomer mixture, IrC₅₄H₃₉N₆ 3/4CH₂Cl₂): C65.2%, H 3.8%, N 7.9%, Cl 5.0; found: C 64.8%, H 4.0%, N 8.1%, Cl 4.9%.

Optical spectroscopy: λ=467 nm (fac/mer isomer mixture, main maximum ofthe powder)

DTA (fac/mer isomer mixture): Rapid decomposition occurred at about 350°C. when the measurement was carried out in air. Decomposition of thesample commences at about 380° C. under inert gas. (Measurementconditions: in air: 28.0/5.0 (K/min)/750.0, under inert gas: 30.0/5.00(K/min)/710).

d) Chromatography, Separation of the fac and mer isomers of the IrComplex of the Formula (7)

The TLC (eluent: toluene) shows 2 spots, with the fac isomer running atR_(F)=0.5 and the mer isomer running at about R_(F)=0.35.

0.46 g of the material to be separated were dissolved in toluene withaddition of a small amount of CH₂Cl₂ and heating to about 30-40° C.

The two isomers were subsequently separated chromatographically withsmall fractionation on silica gel (0.063-0.200 mm J. T. Baker) usingtoluene as eluent (dimensions of the column: length: 30 cm, diameter: 6cm).

Amount of fac isomer obtained: 0.2886 g

¹H-NMR (CD₂Cl₂, 500 MHz) (fac):

δ=8.10 (d, 3H), 7.94 (d, 3H), 7.28 (m, 6H), 7.06 (m, 3H), 7.02 (m, 3H),6.74 (m, 3H), 6.68 (m, 3H), 6.60 (d, 3H), 6.56 (d, 3H), 6.42 (d, 3H),6.29 (m, 3H), 6.18 (d, 3H).

mer isomer: 0.0364 g

¹H-NMR (CD₂Cl₂, 500 MHz, −20 ° C.) (mer):

δ=8.30 (d, 1H), 7.89 (m, 2H), 7.73 (d, 1H), 7.56 (d, 1H), 7.31 (d, 1H),7.28-7.16 (m, 5H), 7.08-7.01 (m, 3H), 6.98 (m, 1H), 6.93 (m, 1H),6.85-6.20 (m, 21H), 5.78 (d, 1H), 5.64 (d, 1H).

e) Preparation of an Ir complex (8)

1.51 g (3.7 mmol) of the naphthimidazolium salt together with 40 ml oftoluene were placed in a 100 ml three-neck flask. 7.4 ml of potassiumbis(trimethylsilyl)amide (0.5 M in toluene, 3.7 mmol) were added at RTover a period of 30 minutes and the mixture was stirred at roomtemperature for 30 minutes. 310 mg (0.46 mmol) of[(μ-Cl)(η⁴-1,5-cod)Ir]₂ were dissolved in 30 ml of toluene and the saltmixture was added dropwise at room temperature. The mixture was stirredat room temperature for one hour, then at 70° C. for two hours and thenovernight under reflux. The mixture was evaporated to dryness and thebrown residue was subjected to purification by column chromatography.This gave a light yellow powder (0.37 g, 35%).

¹H-NMR (fac/mer isomer mixture, data for the main isomer (fac isomer)):(CD₂Cl₂, 500 MHz): δ=8.47 (s, 1H), 8.05 (m, 2H), 7.57 (d, 1H), 7.41 (m,1H), 7.33 (d, 1H), 7.28 (t, 1H), 7.09 (m, 1H), 6.75 (s, 1H), 6.69 (d,1H), 6.64 (t, 1H) 6.57 (d, 1H), 6.52 (m, 1H), 6.24 (m, 2H).

¹³C-NMR (fac/mer isomer mixture, data for the main isomer (fac isomer)):(CD₂Cl₂, 125 MHz): δ=193.9 (NCN), 146.67, 137.6, 136.9, 131.4, 129.5,128.4 (C), 135.7, 128.2, 127.5, 127.4, 127.3, 127.0, 126.8, 126.7,124.2, 124.0, 123.7, 120.7, 111.8, 106.2, 105.4 (CH).

Mass (EI): m/e=1151 (M-H⁺).

Elemental analysis (fac/mer isomer mixture, IrC₆₉H₄₅N₆ 1/2CH₂Cl₂): C70.0%, H 3.9%, N 7.1%, Cl 5.0; found: C 69.9%, H 4.2%, N 7.0%.

-   -   DTA: decomposition occurred above about 360° C. in the        measurement in air (measurement conditions: 35.0/5.0        (K/min)/720.0).

f) Crystal Structure Analysis of the fac isomer of the Ir Complex (7)

Crystals suitable for X-ray structure analysis were obtained under aninert gas atmosphere by slow diffusion of pentane into a solution of afac/mer isomer mixture of the Ir complex (7) in methylene chloride. FIG.2 shows the crystal structure of the fac isomer of the Ir complex (7).The lengths of the Ir-carbene carbon bonds of the three ligands are2.034 Å, 1.997 Å and 2.025 Å and thus each correspond to an Ir—C singlebond. The pairing of in each case two molecules of the Ir complex (7)via one of the fused-on phenyl rings of each is conspicuous. The averagedistance between the participating phenyl ring planes is 3.6 Å.

g) Optical Spectroscopy of the Ir Complex (7) ga) Measurement of OpticalProperties as a Function of the isomer Ratio

Samples of the Ir complex (7) were measured in a concentration of 2 mg/lin toluene (“spectroscopic grade”). Various samples having differentfac-mer isomer ratios were examined.

gaa) Samples

The following samples having different isomeric purities werecharacterized in terms of their optical properties (table 1) andcompared below.

TABLE 1 Composition of the samples for optical spectroscopy Sample #fac/mer ratio 1 from example 2c 9:1^(a) 2 removal of the fac isomer by2:1^(a) sublimation ^(c)) 3 by column 29:1^(b)  chromatography 4(example 2d)  1:37^(b) ^(a)Ratio according to ¹H-NMR ^(b)Ratio accordingto HPLC ^(c)Sublimation is carried out in a high vacuum unit(preliminary diaphragm pump, molecular turbopump) at p = 1 × 10⁻⁵ mbar.The appropriate amount of the substance was placed in a reservoir, theapparatus was carefully evacuated and the temperature was graduallyincreased. The sublimation was carried out as a fractional sublimation.

gab) Absorption Spectra of the Ir Complex (7) in Toluene

Normalized absorption spectra of the samples 1 to 4 in toluene weremeasured. The spectra of the crude Ir complex (7) (sample 1) and sample2 in toluene solution cannot be distinguished. The fac isomer (sample 3)is hypsochromically shifted by 6 nm compared to the mer isomer (sample4) and clearly shows a shoulder at 335 nm. Mathematical superposition ofthe fac and mer spectra in a ratio of 80/20 is virtually identical tothe absorption spectrum of the starting sample (sample 1). This confirmsthat the starting mixture comprises the two isomers in the weightedratio z_(fac)/z_(mer) of 80/20.

A normalized absorption spectrum corresponds to the measured opticaldensity relative to the optical density at the absorption maximum; it isconcentration-independent and describes only the line shape.

${{OD}_{i}^{norm}(\lambda)} = {\frac{{OD}_{i}(\lambda)}{{OD}_{i}^{\max}\left( \lambda_{\max} \right)} = \frac{ɛ_{i}(\lambda)}{ɛ_{i}^{\max}}}$

In the mathematical superposition:

$\begin{matrix}{{{OD}_{cal}^{norm}(\lambda)} = {\frac{{{OD}_{fac}^{\max}\mspace{14mu}{{OD}_{fac}^{norm}(\lambda)}} + {{OD}_{mer}^{\max}\mspace{14mu}{{OD}_{mer}^{norm}(\lambda)}}}{{OD}_{fac}^{\max} + {OD}_{mer}^{\max}}N_{norm}}} \\{= {\left( {{z_{fac}\mspace{14mu}{{OD}_{fac}^{norm}(\lambda)}} + {z_{mer}\mspace{14mu}{{OD}_{fac}^{norm}(\lambda)}}} \right)N_{norm}}}\end{matrix}$${{{where}\mspace{14mu} z_{fac}} + z_{mer}} = {{1\mspace{14mu}{and}\mspace{14mu} z_{fac}} = \frac{{OD}_{fac}^{\max}}{{OD}_{fac}^{\max} + {OD}_{mer}^{\max}}}$

The values z_(fac) and z_(mer) are the proportions weighted according tothe optical density at the absorption maximum and depend on the productof the maximum molar extinction coefficient ε_(max) and theconcentration. They are not identical to the mole fractions. These canbe obtained from z_(fac) and z_(mer) with the aid of the extinctioncoefficients at the absorption maximum ε_(max) (fac and mer). The ratioz_(fac)/z_(mer) is the ratio of the optical densities at the absorptionmaxima. N_(mer) is the normalization factor which guarantees that thesummated spectrum is normalized to one.

gac) Emission Spectra of the Ir Complex (7) in Toluene

Normalized emission spectra of the samples 1 to 4 in toluene weremeasured. In the emission spectra, fac and mer isomers are clearlydistinguishable in terms of shape and position of the maxima. The merspectrum is clearly shifted bathochromically (emission maxima 395 vs.461 nm). The contribution of the mer isomer in the mixture is shown bythe shoulder at 450 nm in the emission spectrum. The emission band ofthe fac isomer is significantly narrower. Here too, mathematicalsuperposition of the normalized emission spectra of the two isomers in aratio of 80/20 gives the spectrum of the starting sample.

In the mathematical superposition of normalized emission spectra:

$\begin{matrix}{{I_{norm}^{em}(\lambda)} = \frac{{{{OD}_{fac}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{fac}\mspace{14mu}{I_{fac}^{norm}(\lambda)}} + {{{OD}_{mer}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{mer}\mspace{14mu}{I_{mer}^{norm}(\lambda)}}}{{{{OD}_{fac}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{fac}} + {{{OD}_{mer}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{mer}}}} \\{= {\left( {{{y_{fac}\left( \lambda_{exc} \right)}\mspace{14mu}{I_{fac}^{norm}(\lambda)}} + {{y_{mer}\left( \lambda_{exc} \right)}\mspace{14mu}{I_{mer}^{norm}(\lambda)}}} \right)N_{norm}\mspace{14mu}{where}}}\end{matrix}N_{norm}$${{y_{fac}\left( \lambda_{exc} \right)} + {y_{mer}\left( \lambda_{exc} \right)}} = {{1\mspace{14mu}{and}\mspace{14mu}{y_{fac}\left( \lambda_{exc} \right)}} = \frac{{{OD}_{fac}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{fac}}{{{{OD}_{fac}\left( \lambda_{exc} \right)}\mspace{14mu}\Phi_{fac}} + {{{OD}_{mer}\left( \lambda_{exc} \right)}\mspace{11mu}\Phi_{mer}}}}$

The values y_(fac) and y_(mer) depend on the excitation wavelength andindicate the proportions of the total emission weighted according to theemission intensity (=product of absorption at the excitation wavelengthOD (λ_(exc)) and quantum yield ϕ). They are not identical to the molefractions. These can be obtained from y_(fac) and y_(mer) with the aidof the extinction coefficients at the absorption maximum ε_(max) (facand mer) and the quantum yields of the two isomers. N_(mer) is thenormalization factor which guarantees that the summated spectrum isnormalized to one.

The measured photoluminescence quantum yields of the four samples intoluene do not vary, both in air-saturated solution and under nitrogen(table 2).

TABLE 2 Quantum yields of the photoluminescence of the Ir complex (7) intoluene. QY¹⁾/%, air- QY¹⁾/%, nitrogen- saturated toluene saturatedtoluene Exc²⁾ 325 nm Exc²⁾ 325 nm Sample 1 0.6 1.3 Sample 2 0.6 1.4Sample 3 (fac) 0.6 1.3 Sample 4 (mer) not determined 1.4 ¹⁾QY = quantumyield ²⁾Exc = excitation wavelength

Compared to measurements in a solid matrix (for example PMMA ordiphenyldi-o-tolylsilane (UGH 1)), the emitter displays a luminescencequantum yield in nitrogen-saturated solution which is smaller by anorder of magnitude. This influence of quenching by solvent molecules isalso reflected in the luminescence decay times of the Ir complex (7): intoluene, nitrogen-saturated: 26.5 ns or 25.8 ns vs. 10% of the complex(7) in UGH 1: 234 ns. The low sensitivity to oxygen is conspicuous. Thiscan be explained by the luminescence decay time in toluene which isshort for a triplet emitter. Given the solubility of oxygen in toluene(1.97 10⁻³ mol/l) and a decay time of about 26 ns, the bimolecularquenching by oxygen is not very effective. However, the decay time inthe solid of 230-250 ns is quite short for a triplet emitter and pointsto effective spin-orbit coupling.

gad) Measurement of Absorption and Emission Spectra at Different fac/merisomer Ratios of the Ir Complex (7) in PMMA Films

To characterize samples 1 to 4 of the Ir complex (7) further as adiluted solid, corresponding PMMA films were produced. To produce thePMMA film, 2 mg of dye (Ir complex (7), examples 2c and 2d) weredissolved in 1 ml of 10% strength (percent by mass) PMMA solution (PMMAin CH₂Cl₂) and a film was applied to a microscope slide by means of a 60μm doctor blade. The film dries immediately. The measurements in toluene(spectroscopic grade) were carried out at a concentration of 10 mg/l. Toremove the oxygen in the solution, nitrogen (O₂ content <150 ppm) waspassed through the solution for 5 minutes before the measurement andnitrogen was passed over the surface of the liquid during themeasurement. All measurements were carried out at room temperature.

Absorption:

The fac isomer (example 2d) displays a significant hypsochromic shift inthe absorption compared to the mer isomer (example 2d) and has ashoulder at 330 nm. The 80/20 superposition of the fac/mer spectra isidentical to the absorption spectra of the starting sample. A somewhatconspicuous aspect is the increased absorption of sample 2 by 280 nm. Itmust not be forgotten here that the absorption spectra are normalizedspectra which show only the spectral shape and not the absoluteabsorption intensity.

Emission

The emission spectrum of sample 3 is, as before in toluene and in thepowder, significantly narrower and pure blue. Sample 4 has the maximumat 460 nm with a shoulder at 400-410 nm. Here too, a mathematicalsuperposition (80/20) reproduces the spectrum of the mixture.

The spectra in PMMA largely correspond to those in toluene. However,quenching of the phosphorescence emission plays a role in the solutionspectra, which has no influence on the emission spectra but reduces thephotoluminescence quantum yield. Table 3 below shows the quantum yieldsof the 4 samples in PMMA films and the color coordinates.

TABLE 3 Photoluminescence quantum yields and color coordinates in PMMA.QY¹⁾/% in X_(RGB) Y_(RGB) PMMA Exc²⁾ in PMMA in PMMA Sample # 325 nm CIE1931 CIE 1931 Sample 1 19 0.160 0.078 Sample 2 15 0.160 0.080 Sample 3(fac) 17 0.160 0.047 Sample 4 (mer) 11 (exc 330 nm) 0.164 0.165 ¹⁾QY =quantum yield ²⁾Exc = excitation wavelength

The quantum yield of sample 4 is significantly lower than those of the 3other samples. In the case of films and at these numerical values, theaccuracy of the measurement of the quantum yields is in the region of 2percentage points, i.e. significantly less accurate than in solutionbecause a film gives poorer definition compared to a solution because itis less homogeneous.

gae) Summary of the Optical Characterization of Complex (7)

The studies show that the fac isomer and the mer isomer of the Ircomplex (7) differ significantly in terms of their spectroscopicproperties. Fac-(7) has a photoluminescence quantum yield in the solidof about 20%, which is virtually twice as high as that of mer-(7). Whilefac-(7) emits in the pure blue region, the emission of mer-(7) extendsinto turquoise-colored regions. On the basis of the positions of theemission and absorption bands, nonradiated energy transfer from the facto mer isomer should be possible (virtually not at all in the oppositedirection), so that at application-relevant degrees of doping or emittermolecule spacings, any contamination by mer-(7) partly quenches theemission of the fac isomer, independently of the action of the merisomer as a trap for individual charges. The additional mer emissionresulting therefrom has a longer wavelength and is less efficient. Thisinterpretation is supported by the measurement of the concentrationdependence of the Ir complex (7) in PMMA films. The use of isomericallypure compounds of the Ir complex (7) is therefore preferred for theconstruction of devices.

h) Determination of the Quantum Yield and Emission Properties of theComplex (8) in Toluene and PMMA

To produce the PMMA film, 2 mg of dye (Ir complex (8)) were dissolved in1 ml of 10% strength (percent by mass) PMMA solution (PMMA in CH₂Cl₂)and a film was applied to a microscope slide by means of a 60 μm doctorblade. The film dries immediately. The measurements in toluene(spectroscopic grade) were carried out at a concentration of 10 mg/l. Toremove the oxygen in the solution, nitrogen (O₂ content <150 ppm) waspassed through the solution for 5 minutes before the measurement andnitrogen was passed over the surface of the liquid during themeasurement. All measurements were carried out at room temperature. Atan excitation wavelength of 330 nm, the emitter gives a quantum yield of10% in PMMA and a quantum yield of 3.6% in toluene. The emission maximumin toluene and PMMA is 512 nm. The CIE coordinates in PMMA areX_(RGB)=0.302, Y_(RGB)=0.591.

3. Device Construction

The electroluminescence of the complex (7) (cf. examples 2c, 2d) and ofthe complex (8) (cf. example 2e) were in each case tested in a devicehaving the following layer structure:

3a) Construction of a Device Comprising Complex (7) as Emitter Substance

The ITO substrate used as anode is firstly cleaned by boiling inisopropanol and acetone. At the same time, it is treated withultrasound. Finally, the substrates are cleaned in a dishwasher usingcommercial cleaners for LCD production (Deconex® 20NS and neutralizationagent 25ORGANACID®). To eliminate any remaining organic residues, thesubstrate is exposed to a continuous flow of ozone for 25 minutes. Thistreatment also improves hole injection, since the work function of theITO is increased.

PEDT:PSS (poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate))(Baytron® P VP Al 4083) is subsequently applied to the specimen fromaqueous solution by spin coating. A thickness of 46 nm is obtained. Thisis followed by the emitter layer which is composed of PMMA (polymethylmethacrylate) dissolved in chlorobenzene and the emitter substance(complex (7), example 2c, example 2d). A twenty percent strength byweight solution of PMMA in chlorobenzene is used. The dopant (emitter)is added thereto in various concentrations.

The 28% strength solution gives a thickness of about 61 nm afterapplication by spin coating and the 40% strength solution gives athickness of 77 nm. These solutions were prepared using an isomermixture (fac/mer) of the emitter in which the facial isomer is the maincomponent (example 2c). Furthermore, a 30% strength solution wasprepared using the isomerically pure fac emitter (example 2d). Afterapplication by spin coating, this solution gives a layer thickness of 27nm.

To balance the charge carriers better, 40 nm of BCP(2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline) are then applied byvapor deposition. BCP is known for its good conductivity for electrons,and it also, owing to its low HOMO, blocks holes which can thus leavethe PMMA only with difficulty. Finally, 1 nm of lithium fluoride and 130nm of aluminum are deposited as cathode.

To characterize the component (OLED), electroluminescence spectra arethen recorded at various currents and voltages. In addition, thecurrent-voltage curve is measured in combination with the luminous powerof the emitted light. The luminous power can then be converted intophotometric parameters by calibration with a luminance meter.

The following electrooptical data are thus obtained for theabove-described components (OLEDs):

PMMA External layer Emission Photometric quantum Lumi- Device thicknessmaximum efficiency yield nance 28% of 61 nm 453 nm 0.8 cd/A   1% 30cd/m² complex 7 (fac/mer)¹⁾ 40% of 77 nm 453 nm 0.65 cd/A 0.75% 75 cd/m²complex 7 (fac/mer)¹⁾ 30% of 27 nm 400 nm 0.53 cd/A  1.5% 80 cd/m²complex 7 (pure fac)²⁾ ¹⁾Example 2c ²⁾Example 2d

3b) Construction of a Device Comprising Complex (8) as Emitter Substance

The ITO substrate used as anode is firstly cleaned with isopropanol at30° C. in an ultrasonic bath for 10 minutes and then cleaned withchloroform, likewise at 30° C. in an ultrasonic bath, for 10 minutes.The substrate is then treated in an oxygen plasma for 20 minutes toeliminate any remaining organic residues.

NPD is then vapor-deposited as hole conductor onto the substrate at2×10⁻⁵ mbar and a deposition rate of 0.2 Å/s, so that a layer thicknessof 40 nm is obtained. Complex (8) (example 2e) as 5% strength dopant issubsequently vapor-deposited together with the matrix material CBP. Thethickness of this layer is likewise 40 nm. This is followed by the BCPhole-blocking layer (6 nm) and an electron conductor layer comprisingAlq₃ having a thickness of 20 nm. Finally, a 1 nm thick LiF layer isapplied and the Al electrode is finally vapor-deposited.

A photometric efficiency of 6.4 cd/A at an emission maximum of 513 nm isobtained for the above-described component (OLED). The maximum luminanceis 1487 cd/m².

We claim:
 1. An uncharged transition metal complex of formula (I)

wherein the symbols have the following meanings: M¹ is a metal atomselected from the group consisting of Co, Rh, Ir, Nb, Pd, Pt, Fe, Ru,Os, Cr, Mo, W, Mn, Tc, Re, Cu, Ag and Au in any oxidation state possiblefor the respective metal atom; L is a monoanionic or dianionic ligand; Kis an uncharged monodentate or bidentate ligand selected from the groupconsisting of phosphines; phosphonates and derivatives thereof,arsenates and derivatives thereof, phosphites, CO; pyridines which maybe substituted by alkyl or aryl groups; nitriles and dienes which form aπ complex with M¹; n is the number of carbene ligands, where n is atleast 1 and when n>1 the carbene ligands in the complex of the formula Ican be identical or different; m is the number of ligands L, where m canbe 0 or ≥1 and when m>1 the ligands L can be identical or different; ois the number of ligands K, where o can be 0 or >1 and when o>1 theligands K can be identical or different; wherein at least one carbene inthe complex of formula (I) comprises formula (II)

wherein the symbols have the following meanings: Do¹ is N; Do² is adonor atom selected from the group consisting of C, N, P, O and S; r is1; s is 2 when Do² is C, is 1 when Do² is N or P and is 0 when Do² is Oor S; X is a spacer selected from the group consisting of silylene,alkylene, arylene, heteroarylene and alkenylene; p is 0; q is 0; Y¹ andY² together form an unsaturated bridge between Do¹ and the nitrogen atomN which has at least two atoms of which at least one is a carbon atom;Y³ is

Z′ is CH or N; R^(12′) is an alkyl, aryl, heteroaryl or alkenyl radical,or 2 radicals R^(12′) together form a fused-on ring which may, ifappropriate, comprise one or more heteroatoms, or R^(12′) is a radicalwhich acts as a donor or acceptor; t′ is 0 to 3 and when t>1 theradicals R¹² can be identical or different; R¹ and R² together form abridge having a total of from three to five atoms of which one or twoatoms may be heteroatoms and the remaining atoms are carbon atoms, sothat the group

forms a five- to seven-membered, ring which, if appropriate, maycontain, in addition to the existing double bond, one further doublebond or in the case of a six- or seven-membered ring two further doublebonds and may optionally be substituted by alkyl or aryl groups and may,if appropriate, comprise at least one heteroatom; and R³ is hydrogen oran alkyl, aryl, heteroaryl or alkenyl radical.
 2. The unchargedtransition metal complex as claimed in claim 1, wherein the group

is selected from the group consisting of

wherein the symbols have the following meanings: R⁸, R⁹ and R¹¹ are eachhydrogen, alkyl, aryl, heteroaryl or alkenyl or a substituent which actsas a donor or acceptor; R¹⁰ is alkyl, aryl, heteroaryl or alkenyl or 2radicals R¹⁰ together form a fused-on ring, or R¹⁰ is a radical whichacts as a donor or acceptor; v is from 0 to 4 and when v is 0 the fourcarbon atoms of the aryl radical in the formula c which are optionallysubstituted by R¹⁰ bear hydrogen atoms.
 3. The uncharged transitionmetal complex as claimed in claim 1, wherein the group

denotes the structure

wherein the symbols have the following meanings: Z is CH or N and can belocated in the o, m or p position relative to the point of linkage tothe group

R¹² is an alkyl, aryl, heteroaryl or alkenyl radical, or 2 radicals R¹²together form a fused-on ring which may, if appropriate, comprise one ormore heteroatoms, or R¹² is a radical which acts as a donor or acceptor;and t is 0 to 3 and when t>1 the radicals R¹² can be identical ordifferent.
 4. The uncharged transition metal complex as claimed in claim1, wherein the structure of formula (II) is selected from the groupconsisting of

wherein the symbols have the following meanings: Z, Z′ are identical ordifferent and are each CH or N; R¹², R^(12′) are identical or differentand are each an alkyl, aryl, heteroaryl or alkenyl radical, or 2radicals R¹² or R^(12′) together form a fused-on ring which may, ifappropriate, comprise at least one heteroatom, or R¹² or R^(12′) is aradical which acts as a donor or acceptor; t and t′ are identical ordifferent and are each from 0 to 3, and when t or t′>1 the radicals R¹²or R^(12′) can be identical or different; R⁸, R⁹ and R¹¹ are eachhydrogen, alkyl, aryl, heteroaryl or alkenyl or a radical which acts asa donor or acceptor; R¹⁰ is alkyl, aryl, heteroaryl or alkenyl or 2radicals R¹⁰ together form a fused-on ring which may, if appropriate,comprise at least one heteroatom, or R¹⁰ is a radical which acts as adonor or acceptor; and v is from 0 to 4 and when v is 0 the four carbonatoms of the aryl radical in the formula c which are optionallysubstituted by R¹⁰ bear hydrogen atoms.
 5. An organic light-emittingdiode comprising at least one uncharged transition metal complex offormula (I)

wherein the symbols have the following meanings: M¹ is a metal atomselected from the group consisting of Co, Rh, Ir, Nb, Pd, Pt, Fe, Ru,Os, Cr, Mo, W, Mn, Tc, Re, Cu, Ag and Au in any oxidation state possiblefor the respective metal atom; L is a monoanionic or dianionic ligand; Kis an uncharged monodentate or bidentate ligand selected from the groupconsisting of phosphines; phosphonates and derivatives thereof,arsenates and derivatives thereof, phosphites, CO; pyridines which maybe substituted by alkyl or aryl groups; nitriles and dienes which form an complex with M¹; n is the number of carbene ligands, where n is atleast 1 and when n>1 the carbene ligands in the complex of the formula Ican be identical or different; m is the number of ligands L, where m canbe 0 or ≥1 and when m>1 the ligands L can be identical or different; ois the number of ligands K, where o can be 0 or ≥1 and when o>1 theligands K can be identical or different; wherein at least one carbene inthe complex of formula (I) comprises formula (II)

wherein the symbols have the following meanings: Do¹ is N; Do² is adonor atom selected from the group consisting of C, N, P, O and S; r is1; s is 2 when Do² is C, is 1 when Do² is N or P and is 0 when Do² is Oor S; X is a spacer selected from the group consisting of silylene,alkylene, arylene, heteroarylene and alkenylene; p is 0; q is 0; Y¹ andY² together form a bridge between Do¹ and the nitrogen atom N which hasat least two atoms of which at least one is a carbon atom; Y³ is

Z′ is CH or N; R^(12′) is an alkyl, aryl, heteroaryl or alkenyl radical,or 2 radicals R^(12′) together form a fused-on ring which may, ifappropriate, comprise one or more heteroatoms, or R^(12′) is a radicalwhich acts as a donor or acceptor; t′ is 0 to 3 and when t>1 theradicals R¹² can be identical or different; R¹ and R² together form abridge having a total of from three to five atoms of which one or twoatoms may be heteroatoms and the remaining atoms are carbon atoms, sothat the group

forms a five- to seven-membered, ring which, if appropriate, maycontain, in addition to the existing double bond, one further doublebond or in the case of a six- or seven-membered ring two further doublebonds and may optionally be substituted by alkyl or aryl groups and may,if appropriate, comprise at least one heteroatom; and R³ is hydrogen oran alkyl, aryl, heteroaryl or alkenyl radical.
 6. A light-emitting layercomprising at least one transition metal complex according to claim 1.7. An organic light-emitting diode comprising a light-emitting layeraccording to claim
 6. 8. A device selected from the group consisting ofstationary visual display units of computers, televisions, visualdisplay units in printers, kitchen appliances and advertising signs,lighting units, and information signs; and mobile visual display unitsin mobile telephones, laptops, vehicles and destination displays inbuses and trains, comprising an organic light-emitting diode as claimedin claim
 5. 9. A method of coloring a polymeric material comprisingadding an uncharged transition metal complex as claimed in claim 1 tosaid polymeric material.
 10. The uncharged transition metal complex asclaimed in claim 1, wherein the structure of formula (II) is coordinatedto a Pt(II) metal atom having a coordination number of
 4. 11. An organiclight-emitting diode comprising at least one transition metal complexaccording to claim
 1. 12. The compound of claim 1, wherein: M is Pt; Mis Pt and n is 1.